In this study the effects of HfB2 addition were investigated on the sintering behavior, densification and microstructure of ZrB2-SiC in the presence of B4C and MoSi2 as a sintering catalyst. 5, 10, 15 and 20 wt% of HfB2 was substituted with ZrB2 in ultra-high temperature ceramic composites of ZrB2-SiC. Additionally, the effect of using nano-scale against common micron size SiC was compared. All compositions were sintered for 1 h in 2100 °C and 2150 °C. Relative and bulk density and open porosity percentage of samples were calculated by Archimedes method. Dimensional changes of pellets and their weight reduction after pyrolysis and sintering proved that increasing of HfB2 leads to increasing... 

The combined effects of SiC and carbon additives on the densification, structure and characteristics of pressureless sintered ZrB2-SiC ceramic composites were studied. The ZrB2-SiC (1-10wt%) composite powders were mixed by 1-2wt% carbon. The prepared powder mixtures were then cold-consolidated and sintered in argon environment in the temperature range of 1800-2100°C for 2h. The constituted phases and microstructural evolutions were studied using x-ray diffraction and scanning electron microscope equipped with an energy dispersive x-ray detector. The obtained results concluded that the densification was increased by extending the sintering time and also by prior holding... 

In this research, the pressureless sintering of ZrB 2 composites were studied to obtain the highest densification and investigate the effects of TiC (2–10% wt) and graphite (1–2% wt) additives on the sinterability. The results showed that by adding TiC, the porosity and water absorption of the samples decreased, resulting in an increase in the density of the samples up to ~98% of the theoretical density. The addition of graphite and TiC reduced the surface oxide layers, improved the density and prevented the grain growth. The graphite additive reacted with B 2 O 3 and ZrO 2 and allowed the system to achieve a complete densification at 2000 °C. Both TiC and graphite additives were completely...