Residual Stress Determination of Multi-pass Welding Process, Stress Relieving Procedures and Its Effect on Crack Propagation
, M.Sc. Thesis Sharif University of Technology ; Farahi, Gholamhossein (Supervisor)
Abstract
One of the most important issues in welding is residual stresses. It is desirable to produce less residual stresses when possible and to reduce them which remain in the structure. At the present, various methods have been developed to reduce the residual stresses. The most important methods are heat treatment, shot peening, and grinding. The main problem in using these methods is cost, and for large structures these methods are often impractical. In recent decades, a technique called vibratory stress relief has been developed. It is used for large structures without limitation of size and weight; besides, the cost of this process is much less in comparison with other conventional methods...
, M.Sc. Thesis Sharif University of Technology ; Movahedi, Mojtaba (Supervisor)
Abstract
Martensitic stainless steels with high strength, good corrosion resistance and formability in the annealed condition are good choices for automotive applications, but they suffer from low weldability due to high hardenability and formation of brittle martensite without tempered structure in the weld metal and heat affected zone (HAZ). In other word, martensitic stainless steels have the worst weldability among all kinds of stainless steels. On the other hand, resistance spot welding is the main method for joining sheets in the automotive industry. Therefore, in the present work, microstructure and mechanical properties of the resistance spot welds of AISI 420 martensitic stainless steel in...
Designing of CK45 carbon steel and aisi 304 stainless steel dissimilar welds
, Article Materials Research ; Vol. 17, issue. 1 , Oct , 2014 , p. 106-114 ; 15161439 ; Hamedi, M ; Kokabi, A. H ; Nazari, A ; Sharif University of Technology
Abstract
Gas tungsten arc welding of CK45 and AISI304 stainless steel was performed through preparation of different types of samples using ER308L and ERNi-1 wires. Welded samples were studied by different techniques including optical metallography, scanning electron microscopy equipped with energy dispersive X-ray spectroscopy (SEM-EDS), X-ray diffraction, hardness measurements and impact test. It was observed that in the buttered specimen, the structure of the weld metal was completely austenitic while the microstructure of unbuttered sample was duplex ferritic-austenitic. M23C6-type carbides were observed within the weld metal of both as-weld specimen types. Effects of different post-weld heat...