Titanium dioxide nanopowders were synthesized by the diffusion controlled sol-gel process (LaMer model) and characterized by DTA-TG, XRD, and SEM. The prepared TiO 2 nanoparticles have uniform size and morphology, and the phase transformation kinetics of obtained material was studied by interpretation of the X-ray diffraction patterns peaks on the base of Avrami equation. The stating point of anatase-rutile phase transformation temperature in the prepared nanoparticles was found between 100 and 200 C. A decreasing trend on the intensity of X-ray peaks of anatase phase was observed up to 600 C when the presence of the rutile phase became predominant. Results indicated that the transition... 

TiO2 nanoparticles were prepared by the sol - gel process using 2-hydroxylethy- lammonium formate as an ionic liquid. Nanoparticles were crystallized at various temperatures (300-700°C). The products were characterized using X-ray diffraction (XRD), nitrogen adsorption - desorption isotherms and scanning electron microscopy (SEM) techniques. It was found that the resulting TiO2 nanoparticles had good thermal stability either to resist collapse or the anatase-to-rutile phase transformation during heat treatment. The photocatalytic activity of the nanocrystalline TiO2 was evaluated by the degradation of Acid Blue 92 (AB92) which is commonly used as a textile dye. The results showed that the... 

Low-temperature perovskite-type cadmium titanate (CdTiO3) with a nanocrystalline and mesoporous structure was prepared at various Ti:Cd molar ratios by a straightforward particulate sol-gel route. The prepared sols had a narrow particle size distribution, in the range 23-26 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained a mixture of ilmenite-CdTiO3, perovskite-CdTiO3, anatase and rutile phases, depending on the annealing temperature and the Ti:Cd molar ratio. Perovskite-CdTiO3 was the major type obtained from cadmium-prominent powders at low temperature, whereas ilmenite-CdTiO3 was the major type obtained from titanium-prominent powders...