Finemet soft magnetic alloy has been in the focus of interest in the last years due to its high saturation magnetization, high permeability and low core loss. The great quantity of papers has been devoted to the study of its structural and magnetic properties, confirms this claim. This paper reviews the different researches performed on Finemet up to now. The criteria that should be satisfied in order to have the high glass forming ability in an alloy and also the techniques applied for production of Finemet ribbons, powders and bulk samples have been explained. In addition, the mechanism of devitrification, nanocrystallization and magnetic softness in this applicable magnetic alloy has been... 

Strontium hexaferrites with the composition of SrFe12−xTix/2Znx/2O19 (x = 0–2.5 in steps of 0.5) were synthesized using chlorides by means of co-precipitation route. The structural, magnetic and microwave absorption properties of the samples were surveyed. The results confirmed that the magnetoplumbite single phase was obtained for all samples and the hexagonal particles dispersed within size range of 1–2 µm. With increasing amount of dopant, coercivity decreased from 5640 to 1486 Oe while the maximum saturation magnetization was 63 emu/g and belonged to x = 0.5. The reflection loss results denoted that the prepared composites had excellent microwave absorption properties and the maximum... 

Superparamagnetic ZnFe2O4/reduced graphene oxide (rGO) composites containing ZnFe2O4 nanoparticles (with ∼5-20 nm sizes) attached onto rGO sheets (with ∼1 μm lateral dimensions) were synthesized by hydrothermal reaction method. By increasing the graphene content of the composite from 0 to 40 wt%, the size as well as the number of the ZnFe2O4 nanoparticles decreased and the saturated magnetization of the composites reduced from 10.2 to 1.8 emu/g, resulting in lower responses to external magnetic fields. Concerning this, the time needed for 90% separation of ZnFe2O4/rGO (40 wt%) composite from its solution (2 mg/mL in ethanol) was found 60 min in the presence of an external magnetic field (∼1... 

M-type Ce–Co substituted barium hexaferrite nanoparticles were synthesized by sol–gel auto-combustion route. The general formula of ferrites was Ba1−xCexFe12−xCoxO19 in which the x was considered to be: x = 0, 0.1, 0.2, and 0.3. The formed phases in the samples were characterized by using X-ray diffraction, Fourier transform infrared spectroscopy, Mössbauer spectroscopy and vibrating sample magnetometer. The results indicated that an increase in substitutional ion amount caused to decrease vibration frequencies of Fe–O band in the tetrahedral site due to the substitution of heavier Co2+ ion for Fe3+ ion in the tetrahedral site. Moreover, some of Ce3+ ions was transformed to Ce4+ and... 

Barium hexaferrite (BaFe12O19) nanoparticles were synthesized by sol–gel auto-combustion route. Prepared samples were sintered at 950 and 1100 °C with Fe3+/Ba2+ = 12 and 20 mol ratio. The formation mechanism of barium hexaferrite was investigated by using X-ray diffraction (XRD) and differential scanning calorimetry (DSC) analyses. In addition, the effect of temperature and Fe3+/Ba2+ mole ratio on BaFe12O19 formation and magnetic properties, and the effect of increasing the Fe3+/Ba2+ upon gel ignition and subsequent phase development were investigated. Finally the magnetic behavior was monitored with VSM. DSC studies showed that pure barium hexaferrite phase was formed from maghemite... 

The multifunctional nanostructures with superparamagnetic and luminescent properties undergo revolution in the field of bio-nanotechnology. In this article, we reported a facile and efficient one-step modified co-precipitation method to load superparamagnetic Fe3O4 nanoparticle on oxidized nanodiamond (Ox-ND). Subsequently, the as-prepared Ox-ND/Fe3O4 hybrid nanoparticle was surface functionalized with vinyltrimethoxysilane (VTMS) to enhance its compatibility with organic media. The structure, morphology, magnetic, and optical properties of the nanohybrid were systematically investigated. The results confirmed successful loading of crystalline Fe3O4 on the surface of Ox-ND. Ox-ND/Fe3O4... 

In present research six samples of nano X-type hexagonal ferrites with general formula SrBaMg2-xCoxDyyFe28-yO46 (x = 0–1; y = 0–0.1 with step size of 0.2 and 0.02, respectively) were synthesized by sol–gel technique. The temperature required for the phase formation of these materials was estimated using thermogravimetric analysis. X-ray diffraction patterns revealed the pure phase of the prepared materials up to the doping concentration of x = 0.4, y = 0.04 along with the second phase for higher doping concentration. The secondary phase appeared due to the solubility limit of higher ionic radius Dy3+ ions into the hexagonal lattice. The mean crystalline size decreased from 29 to 18 nm while... 

Ca-doped Ni–Mg–Mn spinel ferrites with compositions of Ni0·5Mg0·3Mn0.2CaxFe2-xO4 (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) were prepared via sol-gel auto-ignition technique. TGA/DTA, FTIR, XRD, FESEM, and VSM were employed to evaluate the thermal, spectral, structural, morphological, and magnetic features of Ca-doped Ni–Mg–Mn spinel ferrites. TGA/DTA curves show the weight loss in the sample. This weight loss was attributed to the oxidation and decomposition of the sample contents at a temperature of 500 °C. XRD reveals a single-phase structure of the Ni–Mg–Mn nano ferrites. A single-phase orthorhombic structure was confirmed for Ca-doped Ni–Mg–Mn ferrites. Structural parameters such as lattice... 

The effects of milling time and annealing temperature on phase formation, microstructure and magnetic properties of nickel-cobalt ferrite synthesized from oxide precursors by mechanical alloying were studied. The study of milling time effects on phase formation of milled materials showed that if milling continues up to 55 h, single phase nano-sized nickel-cobalt ferrite is obtained. Also, magnetic properties of powders versus milling time and annealing at different temperatures extensively changed, so that annealing at 1200 °C increased the magnetization saturation of the as-milled powder from 15.1 to 53.6 emu/g. X-ray powder diffraction technique (XRD) with Cu-Ka radiation was employed for... 

The structural, electrical, magnetic and high frequency properties of Ni-substituted Zn2W-type hexagonal ferrites were investigated for microwave applications. Ferrite powders with chemical compositions Ba0 · 5Sr0.5NixZn2-xFe16O27 (where Ni-substitution was varied from 0.0 to 1.5 with a step size of 0.5) were prepared using sol-gel auto-combustion at 1300 °C. X-ray diffraction (XRD) analysis confirmed the single-phase hexagonal ferrite structure. The lengths of both the axis i.e. minor and major (a, c) obtained from hkl values of XRD peaks were decreased with Ni-substitution due to the difference in ionic radius of the substituted metal ions. DC electrical resistivity obtained by two-point... 

Herein, a magnetic zirconium-based metal-organic framework nanocomposite was synthesized by a simple solvothermal method and used as an adsorbent for the removal of direct and acid dyes from aqueous solution. To enhance its adsorption performance, poly(propyleneimine) dendrimer was used to functionalize the as-synthesized magnetic porous nanocomposite. The dendrimer-functionalized magnetic nanocomposite was characterized by field-emission scanning electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, nitrogen adsorption/desorption isotherms, and vibration sample magnetometer. The obtained results revealed the successful synthesis and functionalization of the... 

In this study, the effects of milling time, chemical composition and heat treatment on microstructure and magnetic properties of nanocrystalline Fe-Si (6.5-25 at.% Si) alloys prepared by mechanical alloying have been investigated. The results show that increasing the milling time or the Si content, decreases the lattice parameter and increases the internal microstrain. The prepared powders mainly consist of micron-sized particles with an average grain size of less than 20 nm. The specific saturation magnetization values are slightly less than those of single crystal or conventional Fe-Si alloys and decrease as Si content increases. The coercive force values of the nanocrystalline as-milled... 

In this research, a facile, two-step synthesis of Fe3O4–LCysteine–graphene quantum dots (GQDs) nanocomposite is reported. This synthesis method comprises the preparation of GQDs via hydrothermal route, which should be conjugated to the LCysteine functionalized core–shell magnetic structure with the core of about 7.5-nm iron oxide nanoparticle and 3.5-nm LCysteine shell. LCysteine, as a biocompatible natural amino acid, was used to link magnetite nanoparticles (MNPs) with GQDs. X-ray powder diffraction, Fourier-transform infrared spectroscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray were used to investigate the presence and formation of MNPs, L Cysteine functionalized MNPs,... 

In this research, a facile, two-step synthesis of Fe3O4–LCysteine–graphene quantum dots (GQDs) nanocomposite is reported. This synthesis method comprises the preparation of GQDs via hydrothermal route, which should be conjugated to the LCysteine functionalized core–shell magnetic structure with the core of about 7.5-nm iron oxide nanoparticle and 3.5-nm LCysteine shell. LCysteine, as a biocompatible natural amino acid, was used to link magnetite nanoparticles (MNPs) with GQDs. X-ray powder diffraction, Fourier-transform infrared spectroscopy, X-ray photoelectron spectroscopy, energy dispersive X-ray were used to investigate the presence and formation of MNPs, L Cysteine functionalized MNPs,... 

The size mono-dispersity, saturation magnetization, and surface chemistry of magnetic nanoparticles (NPs) are recognized as critical factors for efficient biomedical applications. Here, we performed modified water-in-oil inverse nano-emulsion procedure for preparation of stable colloidal superparamagnetic iron oxide NPs (SPIONs) with high saturation magnetization. To achieve mono-dispersed SPIONs, optimization process was probed on several important factors including molar ratio of iron salts [Fe 3 and Fe 2], the concentration of ammonium hydroxide as reducing agent, and molar ratio of water to surfactant. The biocompatibility of the obtained NPs, at various concentrations, was evaluated via... 

FeNiCo base powder alloy with nominal composition Fe-27Ni-17Co-4Ti (wt%) was prepared from elemental powders by mechanical alloying. The structure of milled powders was characterized by XRD and SEM. The effect of nanosize structure on magnetic properties and shape memory behavior was studied using VSM and DSC. After milling for 240 minutes by high energy vibrational ball mill under argon atmosphere, supersaturated solid solution formed with mean crystallite size of ∼20 nm. Results of VSM examinations showed that by milling for 240 minutes saturation magnetization and intrinsic coercivity reached 304 emu/gr and 21 Oe, respectively. XRD analyses made it clear that transformation from BCC to... 

Magnetite nanoparticles with a size distribution of 15-21 nm were synthesized and decorated onto surface of graphene oxide by ultrasound assisted precipitation. Size and size distribution of the obtained M-GO hybrid were appreciably finer than the hybrids prepared by stirring method. M-GO is a superparamagnetic material with saturation magnetization of 31 emu g-1. The Langevin equation was successfully applied for estimation of size of Fe3O4 nanoparticles in M-GO hybrid, with maximum error of 17.5%. The study put forward a formation mechanism for M-GO, based on instrumental analyses. Adsorption isotherms of Sr2+ and Co2+ ions, which were fitted by Langmuir monolayer... 

In this study, magnetic nanoparticles (MNPs) were synthesized via co-precipitation method. To enhance the biocompatibility and colloidal stability of the synthesized nanoparticles, they were modified with carboxyl functionalized PEG via dopamine (DPA) linker. Both modified and unmodified Fe3O4 nanoparticles exhibited super paramagnetic behavior (particle size below 20 nm). The saturation magnetization (Ms) of PEGdiacid-modified Fe3O4 was 45 emu/g, which was less than the unmodified Fe3O4 nanoparticles (70 emu/g). This difference indicated that PEGdiacid polymer was immobilized on the surface of Fe3O4 nanoparticles successfully. To evaluate the efficiency of the resulting nanoparticles as...