In this paper, the effects of the multi-walled carbon nanotubes (MWCNTs) and nanographene (GP) on the mechanical performance of the cementitious mortars were investigated in different environments. Six mix designs were fabricated by considering the previous studies and exposed to potable water, acidic, and alkaline environments. The GP and MWCNTs partially replaced the cement with 0.25 %, 0.5 %, and 1 % of its weight. The standard mechanical tests, X-ray diffraction (XRD), and scanning electron microscope (SEM) analysis were performed on the specimens. The results indicated that including the MWCNTs and GP increases the compressive strength by 10 % and 20 % and similarly improves the tensile... 

In this work, asphaltene adsorption in a sandstone core sample under dynamic conditions and during miscible CO2 injection was studied using live oil sample which is close to real conditions in petroleum reservoirs. In order to investigate of damage in sandstone core sample by the deposited material such as asphaltene, the morphology analysis of sandstone core sample using scanning electron microscopic method was studied. Also analyses of the adsorbed material in sandstone core sample by Soxhlet extraction using an azeotrope mixture and with SARA method were performed. The experimental results show that by increasing the flow rate of injected CO2, the amount of asphaltene in retained material... 

In this study, the effect of carboxyl-terminated butadiene-acrylonitrile liquid rubber on fracture toughness of glass-reinforced epoxy composites has been investigated. Fracture toughness tests were conducted in modes I, II and different mixed mode ratios. The data obtained from these tests have been analyzed by using different methods. Results indicated that interlaminar fracture toughness of composite specimens improved considerably through addition of carboxyl-terminated butadiene-acrylonitrile in modes I, II and mixed mode. Interlaminar fracture surfaces of the specimens were also characterized by field emission scanning electron microscope  

It has been found that the high wear resistance of NiTi alloy is mainly attributed to its pseudoelasticity which is only effective within a small temperature range. It is believed that pseudoelasticity becomes ineffective by applying high-load wear condition which yields plastic deformation and temperature increment during wear test. Therefore, the enhanced wear resistance can be obtained from the improvement of mechanical property of the alloy without much reduction of pseudoelasticity. In this study, a low weight percentage of hard Al2O3 nanoparticles were added to NiTi atomized powders. The resultant powder mixture was homogenized by ball milling and sintered in a vacuum furnace in order... 

The feasibility of fabricating relatively monodispersed polymeric nanoparticles by the electrospray method in a modified electrospray set-up is demonstrated in this study. The polymer solution is electrosprayed in the single cone-jet regime through a nozzle. After solvent evaporation, during which particles pave from the nozzle to collector, the fabricated nanoparticles can be collected in deionized water, which plays the role of surfactant for particles, not allowing them to aggregate. The results of scanning electron microscope and dynamic light scattering analysis clearly confirm the fabrication of monodispersed spherical polymeric nanoparticles with diameter range from 80 to 120nm with... 

A two-stage hydrogen-reduction/sintering procedure was used to synthesize W-15 wt%Cu nano-composite tablets. Hydrogen-reduction was carried out at 600, 650, 700 and 750 °C for 15-90 min and sintering was performed at 1100, 1150, 1200 and 1250 °C for 60 min. Morphology and grain size of the products were rigorously investigated by scanning electron microscope (SEM), X-ray diffractometer (XRD) and nano-particle Zeta-sizer. Maximum consolidation of the nano-composite product was achieved at 1200 °C. Hydrogen-reduction at 700 °C for 90 min showed an average particle size of ∼72.9 nm. Total reduction was achieved at higher temperatures and longer times. The mixture had a homogeneous structure... 

A simple method for synthesis of NaxWO3 nanorods and nanobelts on sputtered tungsten films by using sodium in soda lime substrate as the catalyst was reported for the first time. After thermally post annealing thin films in a temperature range of 600-750 °C in N2 ambient for 80 min, crystalline NaxWO3 nanorods and nanobelts with [001] direction were formed depending on the annealing temperature. Experimental results reveal that the annealing temperature at 700 °C is the optimum temperature for the growth of sodium-doped tungsten oxide nanorods with maximum density on the surface. According to scanning electron microscopic observations, the synthesized nanorods are ∼50 nm in width and a few... 

In recent years, the autoclaved aerated concrete (AAC) has been widely used in the building construction industry, especially for construction of infill walls. However, the AAC suffers from several drawbacks such as low compressive and tensile strength, high water absorption as well as insufficient resistance against impacts. To address such issues, this study evaluates the mechanical properties of the AAC blocks in which, the cement has been replaced with nano-graphene. For this purpose, various replacement ratios (0.2, 0.4, and 0.8) were selected and different tests such as compressive and tensile strength (cylindrical specimens with the size of 10 × 20 cm), impact resistance and water... 

The mixed nano-ferrites materials Cu0.6Zn0.4HoxFe2−xO4 (0.00 ≤ x ≤ 0.12) were prepared via the sol–gel auto combustion technique. The TGA curve established the annealing temperature (500 °C) for phase formation. The single exothermic peak on the DSC plot occurred at 341 °C temperature. XRD patterns of these nano ferrites verified single phase formation of the FCC cubic structure. The lattice constant a was increased from 8.4244 to 8.4419 Å and then its value decreased to 8.4319 Å. Crystallite size was found in the range of 7 to 16 nm. The surface morphology of the samples was observed from the scanning electron microscope (SEM) images. The grain size was found within the range of 90 nm to... 

The mixed nano-ferrites materials Cu0.6Zn0.4HoxFe2−xO4 (0.00 ≤ x ≤ 0.12) were prepared via the sol–gel auto combustion technique. The TGA curve established the annealing temperature (500 °C) for phase formation. The single exothermic peak on the DSC plot occurred at 341 °C temperature. XRD patterns of these nano ferrites verified single phase formation of the FCC cubic structure. The lattice constant a was increased from 8.4244 to 8.4419 Å and then its value decreased to 8.4319 Å. Crystallite size was found in the range of 7 to 16 nm. The surface morphology of the samples was observed from the scanning electron microscope (SEM) images. The grain size was found within the range of 90 nm to... 

This study investigates the durability of confined geopolymer concrete with fiber-reinforced polymer and compares the results with ordinary Portland cement concrete (OPCC). Two hundred and seventy geopolymer concrete (GPC) specimens with different mix designs (fly ash- and granulated blast furnace slag(GBFS)-based GPC) were prepared and then wrapped with two different fiber-reinforced polymers (carbon and glass FRPs). For 12,960 hrs (eighteen months), the specimens were exposed to four different pHs (2.5, 7 (water), 7.25 (saltwater), 12.5). The reliability analysis was performed after modeling the compressive strength over time. Based on the results, the ductility of all specimens decreased... 

A new facile strategy for fabrication of high surface area electrode in the form of mixtures of coated carbon nanotubes (CNTs) and TiO2 nanoparticles with various weight ratios is reported. The so-called polymeric gel process was used to deposit thick film containing uniform distribution of TiO2 nanoparticles and coated CNTs with high porosity by dip coating for dye-sensitized solar cells (DSSCs) applications. Based on simultaneous differential thermal analysis, the minimum annealing temperature to obtain inorganic- and organic-free films was determined at 500°C. X-ray diffraction analysis revealed that deposited films were composed of primary nanoparticles with crystallite size in the range... 

Fiber reinforced gypsum are prevalent building materials in which short fibers with high tensile strength are embedded into a gypsum matrix to produce supplemental strong and lightweight construction materials. Due to confrontation to a rising risk of death and economic disaster in earthquake-prone areas, quake-resistant materials and structures should be employed for building constructions. Gypsum based composites as a unique candidate for this purpose reduce the risks and produce much confident construction materials for residential buildings. In this work tensile strength of gypsum composites with different volume fraction of polypropylene (PP) and poly-paraphenylene terephthalamide... 

Titanium anodes coated with noble metal oxides are widely used in chlorate industry. In fact, these anodes are dimensionally stable. In this article, the electrochemical characteristics of the ternary oxide coating created by sol-gel on titanium, which consisted of Ti, Ru and Ir, were investigated in the number of different layers. The electrochemical properties of anodes, morphology of samples, and phase analysis were investigated respectively by cyclic voltammetry and polarization measurements, Field Emission Scanning Electron Microscope (FESEM) and XRD. The result indicated that the application of the more layer number increases the rate of chlorine evolution. Also, The morphology of the... 

Y2 O3:Eu3+ nanostructures with bright red emitting phosphors have been synthesized by the combustion method using water and water/ethanol mixture as solvents. The effect of the solvents on nanostructure and luminescence properties of combustion synthesized Y2 O3:Eu3+ was explored. The synthesized nanostructures were calcined at 400 ° C and 1000 ° C to remove the organic phases and enhance the crystallinity. The crystal structures were characterized by an X-ray diffractometer and the particle size and morphology of the synthesized nanostructures were studies using a field emission scanning electron microscope and a transmission electron microscope. We found that the solvent choice has a... 

The low temperature perovskite-type calcium titanate (CaTiO3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route. The prepared sol had a narrow particle size distribution about 17 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that, the synthesized powders had highly pure and crystallized CaTiO3 structure with preferable orientation growth along (1 2 1) direction at 400-800 °C. The activation energy of crystal growth was calculated 5.73 kJ/mol. Furthermore, transmission electron microscope images showed that the average crystallite size of the powders annealed at 400 °C was around 3.5... 

Hydrocarbon production decline as a result of formation damage caused by fines migration has been widely observed in laboratory corefloods and natural flows in porous media. Permeability impairment due to fines migration is explained by different capture mechanisms of already released particles at some pore sites. Preventing detachment of in-situ particles from the rock surface during enhanced oil recovery (EOR) agent injection into the porous media has been reported recently. In this experimental study, the effect of five types of metal oxide nanoparticles; γ-AI2O3, ZnO, CuO, MgO and SiO: to adsorb the fine particles existing in the flowing suspension has been investigated. In each test,... 

In the present work, we focused on simultaneously control electron injection and electron transport, in dye-sensitized solar cells (DSSCs), aided by introducing Cr3+ and CNTs into a TiO2 photoanode, respectively. X-ray photoelectron spectroscopy (XPS) revealed that, Cr 3+ and CNTs were successfully incorporated into the TiO2 lattice without forming secondary phases. X-ray diffraction (XRD) analysis showed that Cr introduction has perfectly balanced the amount of anatase and rutile phases in order to accomplish a more efficient cell. Field emission scanning electron microscope (FE-SEM) images showed deposited films to have a porous morphology composed of nanoparticles and TiO2 nanoparticles... 

In the present work a new strategy for straightforward fabrication of CdS/CdTe solar cells, containing CdS nanowires and nanoparticles as a window layer and CdTe nanoparticles and microparticles as an absorber layer, are reported. CdS and CdTe nanostructures were synthesized by solvothermal method. X-ray diffraction analysis revealed that highly pure and crystallized CdS nanowires and nanoparticles with hexagonal structure and CdTe nanoparticles with cubic structure were obtained. Atomic force microscope and field emission scanning electron microscope images showed that CdS nanowires with length of several μm and average diameter of 35 nm, CdS nanoparticles with average particle size of 32... 

A new strategy for enhancing the efficiency of TiO2 dye-sensitized solar cells (DSSCs) by design of a new double layer film doped with Cr ions, with various morphologies, is reported. X-ray diffraction and field emission scanning electron microscope (FE-SEM) analyses revealed that the synthesized nanoparticles had uniform and nanometer grains with different phase compositions and average crystallite size in the range of 10-12 nm depending upon Cr atomic percentage. UV-vis absorption showed that Cr introduction enhanced the visible light absorption of TiO2 nanoparticles by shifting the absorption onset to visible light region. Furthermore, the band gap energy of nanoparticles decreased with...