Synthesis and Investigation of Corrosion Resistance and Mechanical Properties of Ni-Fe Multilayer Coatings with SiC Particles
, M.Sc. Thesis Sharif University of Technology ; Ghorbani, Mohammad (Supervisor)
Abstract
Electrochemical deposition of multilayer coatings is one of the surface engineering techniques to create thin surface layers with a controlled structure in order to create desirable surface properties. In this research, the nickel-iron-silicon carbide multilayer coating is deposited from a single bath with a sulfate composition and by changing the current density between two values (10 and 40 mA/cm2). The number of layers in multilayer coating was 4, 8, 16, 32.The effect of current density and the number of layers on chemical composition, surface morphology, phase structure, corrosion resistance, nano hardness measurement, wear resistance of multilayer coatings respectively using electron...
Molten salt synthesis of a SiC coating on graphite flakes for application in refractory castables
, Article Ceramics International ; 2016 ; 02728842 (ISSN) ; Bavand Vandchali, M ; Golestani Fard, F ; Nemati, A ; Sharif University of Technology
Elsevier Ltd
Abstract
A silicon carbide coating was formed on the surface of graphite flakes by reaction of molten Si with carbon at 1100-1300. °C in a 95%KCl-5%NaF molten salt under Ar atmosphere. The effect of temperature and Si/graphite ratio in the initial mixture on the quality and the amount of SiC were investigated by XRD and SEM/EDS analyses. Also, the water wettability, oxidation resistance and zeta potential of un-coated and coated graphite were examined by TGA analysis and sedimentation test. The results show the amount of coating to increase in the coated flakes with increasing temperature and Si/graphite ratio. The SiC coating improves water wettability of graphite and acts as a protective layer to...