Sharif Digital Repository

A long-term antibacterial activity of implants without compromising their biocompatibility is highly desirable to minimize the biomaterial-associated infections. Although tantalum oxide nanotubes (Ta2O5 NTs) are promising coating materials for orthodontics and orthopedics applications, their insufficient antibacterial activity retains vulnerability to post-implantation infections. This study aimed to endow antibacterial characteristics to the Ta2O5 NTs-coated Ti6Al4V substrates by decoration of silver oxide nanoparticles (Ag2O NPs). The well-adherent Ta2O5 NTs were grown via anodization of a pure tantalum (Ta) layer coated by physical vapor deposition (PVD) on the Ti6Al4V substrates. The... 

The nanotubular arrays of titanium dioxide (TiO2 NTs) have recently received considerable interest for fabrication of dental and orthopedic implants. However, their antibacterial activity requires substantial improvement for the potential infections minimization, without compromise of their biocompatibility. In this work, TiO2 NTs were developed on Ti6Al4V substrates via anodization at a constant potential of 60 V for 60 min, followed by heat treatment at 500 °C for 90 min. Physical vapor deposition (PVD) was further employed to decorate silver oxide nanoparticles (Ag2O NPs) on the nanotubular edges. The results indicated that the highly-ordered TiO2 NTs with decorated Ag2O NPs could promote... 

Ag2O particles were loaded on the surface of ZnCr-LDH via an anion-exchange precipitation approach by using privilege of the memory trace feature of the LDH-type materials. The structural properties of the resulted photocatalyst were explored by different spectroscopic and microscopic methods. The photocatalytic studies on acid black degradation ascertained that the prepared Ag2O/ZnCr-LDH nanocomposite represented an observably increased degradation performance of organic pollutants compared with pure Ag2O and ZnCr-LDH. This improved photocatalytic performance can be ascribed to the enhanced surface area, good order distributing of particles and effective charge carrier transfer and... 

Ag and Ni are immiscible, mainly due to their large lattice mismatch. This paper reports on their nanoscale formation of solid solution at room temperature by simple reduction reactions which lead to the amorphous Ag-Ni alloy nanoparticles (ANPs) with mono-disperse distribution. Microscopic and spectroscopic studies confirmed dependence of the alloy composition on size of nanoparticles. In the presence of different ligands such as sodium citrate, polyvinyl alcohol and potassium carbonate a mixture of silver oxide and Ag-Ni ANPs was achieved. Stoichiometry of the Ag-Ni ANPs was also found to be strongly dependent on ligands of the reduction reaction and further study shows without any ligand... 

In this paper, the effect of several different parameters on the thermal resistance of a Closed Loop Pulsating Heat Pipe (CLPHP) has been investigated. These parameters include the working fluid, the inclination angle, the filling ratio and the heat influx. Also, the impact of using nanofluids with different nano-particle concentrations has been analyzed. It was observed that a CLPHP can increase the heat transfer up to 11.5 times compared to an empty pipe. Optimum performance for a system with the water-silver nanofluid was achieved at conditions of 50% filling ratio and 0.9 K/W of thermal resistance, and for the water-titanium oxide system, these optimal conditions were found to be 40%... 

Here in, reduced graphene oxide/g-C3N4/Ag2O nano structure (RGO/CAO) was decorated through a facile and simple chemical method. After that RGO/CAO nano structure combined with poly aniline electrochemically to form a composite electrode. Several physicochemical techniques were applied to characterize the composite electrode such as X-ray Diffraction (XRD), Fourier Transform Infra-Red spectroscopy (FTIR), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). Furthermore, several electrochemical techniques were used to study the performance of composite electrode as an electrochemical capacitor. Results show that RGO/CAO nano... 

Nanocrystalline TiO2-AgO thin films and powders were prepared by an aqueous particulate sol-gel route at the low temperature of 573 K (300 °C). Titanium tetraisopropoxide and silver nitrate were used as precursors, hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the phase composition of the mixed oxide depends upon the annealing temperature, being a mixture of TiO2 and AgO in the range 573 K to 773 K (300 °C to 500 °C) and a mixture of TiO2, AgO, Ag2O at 973 K (700 °C). Furthermore, one of the smallest crystallite sizes was obtained for TiO...