This research investigated the long-term environmental effects on bond strength at the interface between fiber- reinforced polymers (FRPs) and timber. A total of 581 timber specimens were bonded with seven types of FRP sheets (unidirectional and bidirectional glass, carbon, aramid, and hybrids) using a wet lay-up technique. The specimens were exposed to acidic, alkaline, fresh water, and sea water solutions with pH of 2.5, 7, 7.25, 10, and 12.5 for 1, 3, 6, 9, and 12 months. A chamber was also used to simulate ultraviolet radiation after 6 months. A series of single-lap shear tests were then conducted to determine the interfacial bond strength reduction. The results showed that bidirectional... 

This study examined the bond at the interface of masonry bricks and fiber-reinforced polymer when exposed to five environments. Three fabrics (aramid, carbon, and glass) and one type of epoxy resin were used. A total of 375 brick-fiber-reinforced polymer specimens were made using wet lay-up technic and exposed to chemical solutions at four pH values (2.5, 7, 10, and 12.5) and substitute seawater. The effect of dry heat on the bond at the interface was also investigated. Single-lap shear tests were then carried out on the samples after 2, 4, 6, 8, 10, and 13 weeks of exposure. The experimental results indicated that freshwater and seawater had a considerable effect on the bond strength of... 

This research investigated the long-term environmental effects on the bond at the interface between fiber-reinforced polymer (FRP) and a masonry brick. Seven types of FRP fabrics were used and placed on the masonry brick using the wet lay-up technique. Unidirectional and bidirectional fibers made of aramid, carbon, and glass and also combination of these fabrics were used. A total of 525 specimens were exposed to five chemical solutions with pH values of 2.5, 7, 10, 12.5 and substitution sea water for 1, 3, 6, 9 and 12 months. A chamber was also used to simulate the ultraviolent (UV) radiation on the specimens. A series of single-lap shear tests were performed on these specimens to determine...