In this study, soft magnetic composite properties of iron base with insulation magnetite nanoparticles have been studied. First magnetite nanoparticles were prepared by co-precipitation method. The iron and magnetite particles with different weights were dissolved in acetone until the acetone evaporates and the composition uniformity of iron and magnetite powder was obtained. Then press the button on the 4 samples of 400, 600, 800, 1000 MPa, and the weight of Magnetite 1, 3, 5, 7 and 10 percent were cold. X-ray diffraction and scanning electron microscope test results showed that iron and magnetite are homogenous distributed. The measurement of AC magnetic properties also suggest that by... 

In this research, soft magnetic-soft composite of iron-borosilicate was prepared by cold compression and then heat treatment at 850 ° C. In order to prepare the initial mixture, the pure iron powder was mixed with different particles of 2% by weight of borosilicate and pressed at 400, 800 and 1200 MPa, and then subjected to thermal treatment at 850 ° C for one hour. After examining the density, electrical resistance, magnetic properties of DC, the magnetic properties of these materials were studied in the frequency range of 10-1000 kHz at room temperature and at 300 ° C. The results show that increasing the particle size increases the saturation magnetization and magnetism and reduces the... 

Photocatalytic as well as photo-Fenton-like processes are promising and ideal technologies for using solar energy to regenerate energy as well as regenerate and revitalize the environment. In fact, photocatalytic processes are one of the most important chemical methods to reduce energy and environmental crises by converting endless solar energy into pure chemical potential. Photocatalytic processes and photocatalysts based on metal-organic frameworks (MOFs) have attracted special attention in recent years due to their excellent and unique properties such as adjustable structure and optical properties. In fact, metal-organic frameworks, as a group of newly emerged crystalline porous...