In this research, carbon nanotube decorated with Cu nanoparticles (CNT/Cu) was synthesized by a new solvothermal process. Solvothermal treatment of CuSO4 and NaOH was completed in ethanol containing ultrasonically dispersed CNTs at 160 °C for 3 h. In the solvothermal process, Cu nanoparticles were heterogeneously deposited on the surface of COOH-functionalized CNTs through the reduction of the Cu+2 ions. Cu nanoparticles with the size of ≈8 nm on CNTs (and some in the solution) and strong bonding between Cu and CNT were obtained by the used process. Microstructural characterization revealed that the solvothermal method is an appropriate method for producing homogenous CNT/Cu nanostructure.... 

Cadmium sulfide (CdS) with different morphologies was successfully prepared by solvothermal process by controlling the processing parameters, including nature of precursor and solvent, reaction temperature and process time. X-ray diffraction patterns revealed that, in all cases highly pure and crystallized CdS with hexagonal structure were obtained. In addition, it was found that the processing parameters influence on preferable growth direction of CdS nanostructures. Field emission scanning electron microscope analysis showed that CdS nanowires with different aspect ratios were obtained (depending upon the reaction temperature and process time) in presence of sulfur powder and... 

In this study, apatite formation ability on TiO2 nanotubes (TNTs) synthesized by anodizing process were compared with TNTs decorated by MnO nanoparticles. The MnO nanoparticles used for decoration process were fabricated via thermal decomposition method. At first, it was strived to find the optimal condition of anodizing process and the effect of applied voltages (15 V, 20 V, and 25 V) and process times (15 min, 20 min, and 25 min) on the diameter of the synthesized TNTs was investigated. Results of microscopic characterizations showed that the completely uniform structure of nanotubes with a diameter in the range of about 100–130 nm was achieved after 20 min of anodizing process at an... 

Cadmium sulfide (CdS) nanowires and nanorods with different aspect ratios were successfully synthesized by the solvothermal method aided with various solvents, namely ethylenediamine, ethanolamine and triethylene tetraamine. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analyses revealed that, highly pure CdS nanostructures were crystallized with different structures and preferable growth orientations depending on solvent nature. Field emission electron microscope (FE-SEM) images showed that the aspect ratio of CdS nanostructures depends upon the dielectric constant and boiling temperature of solvents. CdS nanostructures with the highest aspect ratio in the form...