6061 aluminum matrix composites containing 30vol% SiC with mean mass particle size of 16 and 22 μm as the reinforcing phase were synthesized by squeeze casting route. The process consisted of fabricating of SiC preform followed by squeeze casting of 6061 aluminum alloy. The SiC preform was made by blending SiC particles with silica as a coal and sintering. The microstructural features, aging behavior, mechanical properties and wear characteristics of the composites were investigated. The results indicated that a homogenous distribution of SiC particles in the aluminum matrix, which is almost free of pores, can be obtained by squeeze casting method. Higher strength and lower wear rates were... 

LM13 alloy is widely used in piston industry, due to its low coefficient of thermal expansion, excellent castability and hot tear resistance. In this research effect of casting process on wear behavior of LM13 alloy was investigated. First, samples were produced using two casting processes and heat treated. Then wear behavior of these samples under dry sliding condition was examined. Results of hardness and strength tests indicated that squeeze cast specimens exhibited higher mechanical properties. Wear experiment results showed that in both squeeze and gravity cast specimens, amount of weight loss increases with increase in sliding distance which is accompanied by reduction in wear rate and... 

There are many approaches to fabricate nanoparticles reinforced aluminum matrix composites. However, uniform distribution of nanoparticle within aluminum matrix remains a difficult challenge. In this study, a novel method is used by taking the advantages from squeeze casting of semi-solid aluminum slurry combined with electromagnetic field to refine the microstructure of the primary Al and eutectic Si phase, plus to obtain uniform distribution nano alumina particles in the aluminum matrix. It is noted that electromagnetic field plays an important role in the formation of non-dendritic primary α-Al particles and a great microstructure refinement occurs as a consequence of the pressure...