The current study was carried out to investigate the kinetics of reactions for the pressure oxidative leaching of a molybdenite concentrate in less than one hour. The effects of oxygen pressure, stirring speed, pulp density, acid concentration and temperature on the leaching rate of the molybdenum were studied. It was found that about 85% of molybdenite was oxidized to molybdic oxide precipitate with remaining molybdenum dissolved in the leaching liquor. Analysis of experimental data showed that the reaction is chemically controlled with activation energy of 68.8 kJ/mol. Furthermore SEM images showed no significant boundary diffusion layer and it was noted that the molybdic oxide... 

This study is concerned with investigation of pressure oxidative leaching of entire molybdenum of a molybdenite concentrate. Effects of oxygen pressure, stirring speed, pulp density, acid concentration, and temperature on the leaching rate of molybdenum were studied. A three-layer feed-forward artificial neural network was applied to model the effect of the abovementioned parameters on the leaching ability. The leaching efficiency was considered as a target value for modeling. The quantified leaching efficiencies obtained by applying different parameters demonstrated a good agreement with neural network predictions  

Kinetics of dissolution of silver present in precious metal scraps in HNO3 was studied in temperature range of 26-85°C. Dissolution rate of silver was much faster than that of copper at all temperatures. Effects of particle size, stirring speed, acid concentration and temperature on the rate of dissolving of silver were evaluated. Dissolution rate decreases with particle size and increases with temperature. Dissolving was accelerated with acid concentrations less than 10 mol/L, Concentrations greater than 10 mol/L resulted in slowing down of the dissolution rate. Shrinking core model with internal diffusion equation t/τ = 1 - 3 (1-x)2/3 + 2 (1-x) could be used to explain the mechanism of the...