Sharif Digital Repository

Foamy Al alloy SiCp composites of different densities ranging from 0.4 to 0.7g/cm3 were manufactured by melt-foaming process, which consisted of direct CaCO3 addition into the molten A356 aluminum bath. Mechanical properties and morphological observations indicated that the three-stage deformation mechanism of typical cellular foams is dominant in the produced A356 aluminum foams. Middle-stage stress plateau shrinkage plus compressive strength and bending stress enhancements were observed in denser foams. With the same Al/SiCp ratio, energy absorption ability and plastic collapse strength of the closed-cell foams were increased with the foam density. Doubling cell-face bending effects...