Sharif Digital Repository

Gas porosities and entrapped double oxide film (hereafter: oxides) are known to be the most detrimental defects in cast Al-Si-Mg alloys. This study investigated the effects of dissolved hydrogen (hereafter: H) and oxides on reproducibility of tensile properties in Al-7Si-0.35 Mg alloys. Also the effects of H and oxides content on the morphology of defects were studied. Four different casting conditions (low oxide-low H, low oxide-high H, high oxide-low H, high oxide-high H) were tested using tensile test bars that were cast in a metallic mold. Results of tensile test that were obtained for each casting condition were analyzed using Weibull two-parameter analysis. Microstructure and fracture...