CdS nanocrystals were thermochemically (thermally activated) synthesized thorough the reaction between CdSO4 and Na2S 2O3 in an aqueous solution. Thioglycolic Acid (TGA) was used as the capping agent and catalyst of the reaction. The method was based on heat activated dissociation of Na2S2O3 and controllable release of S and free electrons in the solution. CdS NCs were formed by heating the sample solution at 96 C for 1 h. The results of optical spectroscopy and transmission electron microscopy demonstrated round shape NCs with sizes about 3.0 nm. The nanocrystals were also luminescent and represented a broad emission with a peak located at 515 nm and FWHM of 160 nm. Several samples were... 

In this work we report a new thermochemical method for the synthesis of ZnS:Mn nanocrystals. Zn(NO3)2 and Na2S 2O3 were used as the precursors and Mn(NO 3)2 was the source of impurity. Thioglycerol (TG,C 3H8O2S) was also used as the capping agent and the catalyst of the reaction. Na2S2O3 is a heat sensitive material which releases S species upon heating. Consequently, the reaction proceeds in temperatures higher than room temperature. The reaction was done in two steps. In the first step, the precursors were heated at 96 °C for an hour without TG. In the second step, TG was injected to the solution and the heating process was continued for longer heating durations. A fast growth occurred in...