Bonding Feasibility, Mechanical Properties and Formability of Three-layered St/AZ31/St Composites Fabricated by Roll Bonding
, M.Sc. Thesis Sharif University of Technology ; Akbarzadeh, Abbas (Supervisor)
Abstract
New materials as hybrid materials or laminate composites, due to combination of many properties, can be used in many industries. The aim of this research is bonding of three-layered St/AZ31/St composite by roll-bonding process. The roll-bonding process was performed at three preheating temperatures, 340, 400 and 450 ⁰C, with thickness reduction of 30 to 68% and different thicknesses of intermediate layer (AZ31). In order to improve the bonding strength, the as-rolled specimens were annealed at constant temperature of 375 ⁰C. For evaluation of bond strength and investigating the formation of a diffusion layer, the results of peel test and microscopic images were studied. Tensile specimens...
Experimental Investigation of Formability and Mechanical Properties of Composites Manufactured by Direct Roll Bonding
, M.Sc. Thesis Sharif University of Technology ; Akbarzadeh, Abbas (Supervisor)
Abstract
In this study, the ST14 low carbon steel sheet was used as a skin layer in the construction of three-layer laminates. The use of this steel was due to its high mechanical properties and excellent formability. A thermoplastic polyurethane sheet was also used as the core layer. The selection criteria of this polymer were no need for adhesive (for bonding metal to polymer) as well as proper mechanical properties (elongation and strength) and physical (density). The perfect process for manufacturing three-layer laminates is the roll bonding process. To manufacturing a laminate with the desired properties of the designer, the rolling parameters (rolling speed and thickness reduction) must be...