Sharif Digital Repository

Self-organised and vertically oriented titanium oxide nanotube array (TNTA) has been synthesised by potentiostat anodisation of Ti foil in fluoride-based electrolyte. By varying the anodisation voltage from 8 V to 24 V it was possible to gradually change the topologies of nanotubes. The size of TNTAs was measured using SEM images and also determined based on a non-destructive optical method. In addition, photoelectrochemical properties of nanotubular TiO2/Ti electrodes were examined by anodic photocurrent response, potentiodynamic polarisation measurements and electrochemical impedance spectroscopy. A general equivalent circuit model was proposed for photoelectrochemical system consists of... 

The major purpose of this research is increasing the photocatalytic activity of TiO2 nanotube arrays by doping with sodium and carbon for using in water splitting as photoanode. The synthesized TiO2 nanotubes (TNA) were characterized using FESEM (Field Emission Scanning Electron Microscope), XRD (X-ray Diffraction), DRS (Diffraction Reflection Spectroscopy) and XPS test (X-ray Photoelectron Spectroscopy) analyses. The results of FTIR and XPS confirmed the presence of sodium and carbon in the lattice of TNA as dopants. Moreover, the DRS test showed the decrease in the band gap energy of TNA from 3.20 to ∼2.88 eV; uv-visible test exhibited extension in the absorption edge of pure TiO2... 

The main purpose of this research work is to investigate the effect of nickel as metal dopant on the morphology and photocatalytic activity of TiO2 nanotube arrays synthesized in the organic electrolyte by anodizing process containing sodium carbonate as an additive (TNAS). In order to characterize the synthesized nanotubes, various analyses such as FESEM, XRD, FTIR, XPS, DRS, and EIS were applied. The results of XPS and FTIR tests evaluate the participation of sodium (Na), nickel (Ni), and carbon (C) in the lattice of nanotubes as dopants. According to the DRS and UV-visible tests results, the band gap energy of TiO2 nanotube arrays decreases from 3.20 to ~ 2.64 eV as well as the absorption... 

The nanotubular arrays of titanium dioxide (TiO2 NTs) have recently received considerable interest for fabrication of dental and orthopedic implants. However, their antibacterial activity requires substantial improvement for the potential infections minimization, without compromise of their biocompatibility. In this work, TiO2 NTs were developed on Ti6Al4V substrates via anodization at a constant potential of 60 V for 60 min, followed by heat treatment at 500 °C for 90 min. Physical vapor deposition (PVD) was further employed to decorate silver oxide nanoparticles (Ag2O NPs) on the nanotubular edges. The results indicated that the highly-ordered TiO2 NTs with decorated Ag2O NPs could promote... 

In the present research, we investigate the synergistic effects of Ru-doping and Ar/H2 reduction treatment on the photoelectrochemical water splitting performance and hydrogen evolution rate of TiO2 nanotube array photoelectrodes. The Ti-Ru alloy with 0.2 at. % Ru was used to grow anodic self-organized Ru-doped TiO2 nanotube layers. An ideal synergy between Ar/H2 reduction treatment and Ru-doping results in the extended absorption toward the visible light region and improved photoelectrocatalytic activity. The black Ru-doped TiO2-x photoanode's water splitting rate improves remarkably (∼ninefold) compared to the black TiO2-x sample (∼twofold). Moreover, the black Ru-doped TiO2-x photoanode... 

Despite the wide application ranges of TiO2, the precise explanation of the charge transport dynamic through a mixed crystal phase of this semiconductor has remained elusive. Here, in this research, mixed-phase TiO2 nanotube arrays (TNTAs) consisting of anatase and 0-15% rutile phases has been formed through various annealing processes and employed as a photoelectrode of a photovoltaic cell. Wide ranges of optoelectronic experiments have been employed to explore the band alignment position, as well as the depth and density of trap states in TNTAs. Short circuit potential, as well as open circuit potential measurements specified that the band alignment of more than 0.2 eV exists between the... 

Electrochemical activity of TiO2 nanotube arrays (NTAs) is restricted by a wide band gap of TiO2. To overcome this restriction, we considered systematic research on two effective methods of doping of TiO2 NTAs such as the N-doping and electrochemical reductive doping and predicting the proper application of them. Band gap narrowing was occurred from 3.16 eV for undoped TiO2 NTAs to 2.9 and 2.7 eV at N-doped and self-doped TiO2 ones respectively. The electrochemical responses of the TiO2 NTAs before and after doping were examined by cyclic Voltammetry (CV) curve. To understand the electrochemical behavior of the undoped and doped TiO2 NTAs, electrochemical impedance spectroscopy (EIS) was... 

TiO2 nanotube arrays (TNA) have been modified by cobalt phosphate (CoPi) through potentiostatic electrodeposition method. Different samples have been prepared by changing the loaded CoPi through the deposition time from 10 to 960 min. Formed catalytic materials have been characterized by different methods. Although charge transfer resistance of the CoPi/TNA photoanodes have been decreased from 5.5 to 4.0 kΩ by increasing the deposition time from 5 to 60 min, the maximum photoresponse was obtained for 10 min CoPi deposition leading to 24% more photocurrent compare to bare TNA which proposed optimum value for cobalt phosphate decoration. Based on field emission scanning electron microscopy... 

Although morphological disorder of nanotube structure is further down than the nanoparticular electrode, its density of traps are the hindering effects in the charge transport. In this study, crack-free TiO2 nanotube membranes, which obtained through a re-anodizing process, are fixed on transparent fluorine–tin-oxide glass by applying a few drops of Titanium Isopropoxide without needing the TiO2 powder paste. Front-side illuminated dye sensitized solar cells fabricated by undoped, N-doped and blue TiO2 nanotube membranes are investigated. The electrical characteristics of TiO2 nanotube based dye sensitized solar cells are followed by theoretical analysis using simple one-diode model.... 

The most common reasons for hard-tissue implant failure are structural loosening and prosthetic infections. Hence, in this study, to overcome the first problem, different bioinspired coatings, including dual acid-etched, anodic TiO2 nanotubes array, anodic hierarchical titanium oxide (HO), micro- and nanostructured hydroxyapatite (HA) layers, and HA/chitosan (HA/CS) nanocomposite, were applied to the titanium alloy surfaces. X-ray diffraction and FTIR analysis demonstrated that the in situ HA/CS nanocomposite formed successfully. The MTT assay showed that all samples had excellent cell viability, with cell proliferation rates ranging from 120% to 150% after 10 days. The HO coating...