A sensitive colorimetric method for the detection of ascorbic acid was proposed in this research based on the reduction of silver ions by ascorbic acid in the presence of citrate-stabilized silver seeds, additional trisodium citrate and a polymer such as polyvinylpyrrolidone. The color of the stable sol is controlled by varying the concentration of trisodium citrate (TSC), polyvinylpyrrolidone, silver nitrate and silver seeds. The reduction of Ag + to triangle silver nanoparticles (Ag-NPs) by ascorbic acid in the presence of trisodium citrate (TSC) and silver seeds produced two very intense surface plasmon resonance peaks of Ag-NPs. The plasmon absorbance of Ag-NPs allows the quantitative... 

The partition constants of l-lysine HCl were measured in polymer-salt aqueous two-phase systems. These systems contain poly(ethylene glycol) with a nominal molecular weight of 4000 or 10000 and two different salts (dipotassium hydrogen phosphate or trisodium citrate 5-hydrate). The experimental data were obtained at temperatures of (293.15, 298.15, and 303.15) K. The effects of temperature, pH, polymer and salt concentrations, polymer molecular weight, and salt type on the partitioning of l-lysine HCl were also studied. The results showed that salt concentration has a significant effect on the partition constant while temperature has less effect. The Diamond and Hsu model was used to... 

In the present study, the electrodeposition of Fe, Pd and Fe-Pd alloys, in alkaline solutions, has been investigated. Using ammonium hydroxide and trisodium citrate as the complexing agents, it has been shown that the co-deposition of Fe and Pd is achieved due to diminishing the difference between the reduction potentials of these two metals. Cyclic voltammetry results clearly show that the electrodeposition processes are diffusion-controlled and the diffusion coefficients of Fe2+ and Pd2+ are 1.11 × 10-6 and 2.19 × 10-5 cm2 s -1, respectively. The step potential experiments reveal that nucleation mechanism is instantaneous with a typical three-dimensional (3D) growth. At low overpotentials,...