This study investigates the tensile properties of various GFRP laminates after exposure to elevated temperatures. Fiber configuration, exposure temperature and laminate thickness were considered as the test variables. A total number of 180 specimens were tested in tension to obtain the mechanical properties of GFRP laminates. Alongside the mechanical tests, SEM analyses were conducted on selected samples before testing to investigate the resin, fiber, and their interface damages. Regardless of the sample type, it was generally observed that the reduction rate in the tensile strength increased with an increase in the exposure time and a decrease in the laminates’ thickness. The results of... 

The use of micromechanical models to study composite material's behavior leads to save time and cost. In this paper, bridging micromechanical models have been used in order to observe the behavior of unidirectional laminate composite under fatigue loading. In order to study the fatigue behavior, stiffness degradation has been studied as well as the strength degradation and a driftnet model has been proposed for each of them. The strength degradation has only been studied for the unidirectional fiber, while the stiffness degradation has been studied for the fibers with different fiber angle. The results are compared with macro-mechanical models and other methods in literature