Sharif Digital Repository

We have investigated segregation of copper at the surface of V 2 O 5 films deposited onto Cu substrate by employing surface analysis techniques. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) confirmed that the Cu is segregated at the surface and its chemical state is Cu 2 O. According to secondary ion mass spectroscopy (SIMS) and glow discharge spectroscopy (GDS), the Cu concentration inside the deposited V 2 O 5 layer is low. Ultraviolet photoelectron spectroscopy (UPS) and scanning tunneling spectroscopy (STS) revealed the segregation alters the surface local density of states. Surface analysis of deposited samples in ultra high vacuum (UHV) condition... 

The present work focuses on the preparation of V2C MXene from Al-V2O5-C mixture heated in a microwave and etched under HF-based process. In the first stage of process, microwave heating caused the formation of an uncommon periodic pattern of V2AlC-Al2O3 MAX phase. In the second stage of process the aggressive leaching (temperature of 80 °C for 96 h) was performed in HF to remove the interlayer aluminum and Al2O3 particles as impurities. The leaching was not completed at room temperature even after 24 h. XRD and FESEM analyses confirmed the successful formation of V2C MXene and its distorted layer, respectively. HRTEM, XPS and Raman analyses also confirmed a perfect structure of V2C MXene. It... 

Oxidative dehydrogenation of propane (ODHP) in a fixed-bed reactor over synthesized vanadia nanocatalysts was investigated physicochemically. Several vanadium pentoxide (V2O5) nanostructures including rod-, belt-, tube-, needle- and flower-like forms were successfully synthesized via reflux and hydrothermal processes utilizing different templates such as monoamines, diamines, aromatic and alcoholic amines. The morphologies of the obtained products were found to be sensitive to the types of templates used. Nanorods obtained were 1.4 μm in length and about 97 nm in width while the VO2(B) nanotubes were of about 76 nm average diameter and up to 1.2 μm long. The diameters of the V2O5 nanotubes... 

V2O5-TiO2 porous layers were synthesized via micro-arc oxidation for the first time. The effect of the applied voltage on morphology, composition, and photo-activity of the layers was investigated. The layers, which consisted of anatase, rutile, and vanadium pentoxide phases, revealed an enhanced photo-activity. About 93% of methylene blue solution was degraded on the synthesized layers after 120 min UV-irradiation with a reaction rate constant of k = 0.0228 min-1. The band gap energies of the vanadia-titania and pure titania layers were calculated as 2.56 and 3.39 eV, respectively  

V2O5/SiO2 catalyst utilized to oxidize the SO2 to SO3 species in the presence of oxygen mainly for producing sulfuric acid. For this catalyst, the active phase was a mixture of vanadium pentoxide and basic sulfate/pyrosulfate material. This active phase at the reaction temperature behaved as a liquid filling up the pores of the silica support. On the other hand, amounts of the SO3 and V5+ species in the catalyst necessarily varied with the concentration of the feed material and temperature rendering complexity to the kinetics of the SO2 oxidation reaction. In the current research, the catalyst preparation with different amounts of such materials was undertaken. Purified Diatomaceous earth of... 

Industrial air pollution from point and nonpoint sources of steel complexes has drawn increasingly more public attention in the past decades. Previous research efforts have been more concentrated on point sources of particulate emissions from these complexes. However, wind-induced particulate emissions from iron ore storage piles not only result in ambient air pollution but also increase economic adverse effects to the industry by loss of process raw materials. Experiments were conducted to assess the impact of wind speed and humidity on particulate emission rates from iron ore storage piles. A wind-generating system and specific iron ore, experimental piles (L:W:H of 30:11.5:5 cm) were... 

Micro-arc oxidation process was used to synthesize V2O5-TiO2 porous layers for the first time. Surface morphology and topography of the layers were investigated by scanning electron microscope (SEM) and atomic force microscope (AFM). X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques were also employed to evaluate phase structure and chemical composition of the layers. It was found that the V2O5-TiO2 layers consisted of anatase, rutile, and vanadium pentoxide phases fraction of which varied with the applied voltage and the electrolyte concentration. It was also revealed that pore size and surface roughness increased with the applied voltage and the electrolyte... 

V2O5-TiO2 layers with a sheet-like morphology were synthesized by micro arc oxidation process for the first time. Surface morphology and topography of the layers were investigated by scanning electron microscope (SEM) and atomic force microscope (AFM). Phase structure and chemical composition of the layers were also studied by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) techniques. It was revealed that the composite layers had a sheet-like structure average thickness of which was about 100 nm depending on the applied voltage. The layers consisted of anatase, rutile, and vanadium pentoxide phases fractions of which varied with the applied voltage. The optical properties... 

In this study, spinel CuCo2O4 (CCO) with a hierarchical hollow sphere morphology was encapsulated in V2O5-decorated ultra-wrinkled graphitic carbon-nitride (VO-UCN) for the first time via a facile glycerol-assisted solvothermal method in the interest of developing a novel high-efficiency double Z-type nano-photocatalyst (denoted as VO-UCN@CCO). The remarkable physicochemical features of the as-prepared nano-photocatalysts were verified using diverse characterization techniques including TGA, XRD, FT-IR, FE-SEM, TEM, BET, UV–vis DRS, PL, EIS, and transient photocurrent techniques. Herein, VO-UCN@CCO nanocomposite was employed for the photodisintegration of levofloxacin (LVOF) antibiotic under...