This study concentrates on the effects of weld sequence and welding fixtures on distribution and magnitude of induced arc welding residual stresses built up in butt-joint of Gas Tungsten Arc Welding (GTAW) AA5251 plates. Aluminum plates have been welded under different welding conditions and then, longitudinal and transverse residual stresses were measured in different points of the welded plates employing hole-drilling technique. The results indicate that welding sequence significantly alters the distributions of both longitudinal and transverse residual stresses while the changing in the weld sequence leads to 44% decrease in longitudinal residual stress. Besides, both the geometry of weld... 

The purpose of this work is to assess the effect of welding fixtures on distributions and values of residual stresses during Gas Tungsten Arc Welding (GTAW). The butt-joint GTAW of AA5251 plate is investigated using a transient thermo-mechanical analysis performed by the finite element program, ABAQUS. The model considers two different welding conditions including unconstrained and perfectly constrained conditions while macro examination and residual stress measurements by implementing hole drilling techniques are utilized to evaluate the predictions. The results show that the utilizing of a welding fixture alters the temperature field within the plate being welded and the depth of the weld... 

Effects of zinc layer on microstructure and mechanical behavior of resistance spot welds of aluminum to galvanized (GS-Al joint) and low carbon steel (PS-Al joint) were explored. The results showed that although nugget 'volume' in PS-Al joint was larger, the nugget 'diameters' of PS-Al and GS-Al joints were almost the same in size since the melted zinc layer was pushed toward the outer regions of the nugget. Melting and evaporation of zinc coat led to reduction of Al-Fe intermetallic layer thickness. Presence of zinc also reduced the fixture-induced tensile stress. Utilizing carbon steel fixtures during welding caused a sensible vibration in the joint members. The vibration resulted in... 

In this work, the thermomechanical responses during the dissimilar friction stir welding of aluminum alloys have been evaluated employing a three-dimensional model and the finite element software ABAQUS. Furthermore, welding experiments have been conducted under different working conditions and the temperature variations during and after welding as well as the produced residual stresses in various positions of the welded samples were measured using hole-drilling technique. The model results were then examined by experimental data, and a reasonable agreement was observed. It is found that tool rotational speed significantly affects the amount of maximum tensile residual stress while traverse...