Sharif Digital Repository

The catalytic activity of Pt/Ni/TiO 2 nanotubes electrode toward glucose has been studied. Fabrication of Pt/Ni nanostructures was done in a single-bath solution through electrochemical pulse method by changing the deposition potential between -0.3 and -4 V vs. SCE, respectively. The resulting modified electrode represented high conductivity due to the effective presence of metallic components and uniform surface area caused by dispersion of Pt and Ni nanostructures. The scanning electron microscopy images also confirmed that a large amount of metals colonies were well-dispersed at the edge of the TiO 2 nanotubes. In addition, the Pt/Ni TiO 2 nanotubes modified electrode exhibited an... 

As an important precursor of crystalline phases, amorphous calcium carbonate (ACC), especially ultrasmall ACC clusters, have been attracting great interest in fundamental research, materials chemistry, as well as industrial applications. However, it is still challenging to synthesize stable ACC clusters in water that can be isolated and concentrated without severe aggregation. Herein, we report a facile dialysis method for producing colloidally stable ACC clusters that are well dispersed in water with the protection of specific polycarboxylic acids, which could be also easily deprotected by small-molecule acids like sodium citrate. Inherent proto-calcite short-range order is found to be... 

As an important precursor of crystalline phases, amorphous calcium carbonate (ACC), especially ultrasmall ACC clusters, have been attracting great interest in fundamental research, materials chemistry, as well as industrial applications. However, it is still challenging to synthesize stable ACC clusters in water that can be isolated and concentrated without severe aggregation. Herein, we report a facile dialysis method for producing colloidally stable ACC clusters that are well dispersed in water with the protection of specific polycarboxylic acids, which could be also easily deprotected by small-molecule acids like sodium citrate. Inherent proto-calcite short-range order is found to be... 

In this study a novel Pt/Ni nanostructure consisting of nano-bushes and nanocubes was fabricated onto TiO 2 nanotubes. The scanning electron microscopy images showed that a large amount of well-dispersed nano-architectures had uniformly covered all over the surface which made an electrode with high surface area. It was obviously seen that the nanocube structures mainly consists of Ni had been grown on top of each other while the Pt colonies represented bush-like structures. As a non-enzymatic glucose biosensor, the Pt/Ni TiO 2 nanotubes modified electrode exhibited an excellent performance. The proposed biosensor had two linear ranges for detection of glucose from 0 to 0.12 mM (correlation... 

Superparamagnetic iron oxide nanoparticles with proper surface coatings are increasingly being evaluated for clinical applications such as hyperthermia, drug delivery, magnetic resonance imaging, transfection, and cell/protein separation. To enhance the applicability of magnetic nanoparticles, two main problems must be overcome. First, as the drug coats the particle surface, a significant portion of it is quickly released upon injection (burst effect). Therefore, only small amounts of the drug reach the specific site after, for example, magnetic drug targeting. Second, once the surface-derivatized nanoparticles are inside the cells, the coating is likely digested, leaving the bare particles... 

Electrophoretic technique was used to deposit micro- and nano-sized aluminum nitride coatings on stainless steel surfaces by using a well-dispersed stable suspension produced by addition of AlN powder plus a small amount of iodine to ethanol. Parabolic regime governed the deposition. Electrophoretic deposition for 240 s at 100 V resulted in formation of a uniformly dense film on the top, but a porous inhomogeneous layer at the bottom. This was attributed to fast deposition of coarse particles and/or agglomerates at large electric fields. After drying, micro-sized particles led to a uniform crack-free interface while nano-particles resulted in fragmented non-cohesive layers. Weight loss... 

Inkjet printing of colloidal metals is an attractive method for direct patterning of electrically conductive structures and interconnects in electronic devices, owing to low-cost, low-waste and simplicity of the process. In the present work, mixtures of well-dispersed silver nanoparticles and ethylene glycol were prepared for the inkjet printing process. Three different surfactants including PVP, MSA and AOT were added to study the stability of the nanosilver colloids. The effect of high-intensity ultrasonic treatment and temperature on the rheological properties was investigated utilising a rheometer in plate-plate geometry. It is shown that the viscosity of the ink increases with...