A series of bifunctional Cu-ZnO-ZrO2/H-Y catalysts of different compositions were prepared by coprecipitating sedimentation method and were characterized by surface area and XRD analyses. The catalytic performance in synthesis of tetrahydrofuran was evaluated and optimized in a three-phase slurry batch reactor. The experimental results showed that the appropriate ratio of Cu/ZnO in the hydrogenation catalyst was 50/45, for which the conversion of maleic anhydride (MA) and selectivity of tetrahydrofuran (THF) reached 100% and 46%, respectively, at 50 bar and 493 K after 6 h of operation. Also, according to these results, it was demonstrated that the incorporation of zirconium oxide in the... 

A technique to achieve the globular weld structure using stirring the localized semisolid zone during butt-joining of zinc AG40A (Zamak-3) die cast alloy is reported. Since the semisolid temperature range of this alloy is very narrow, the accurate controlling of weld pool temperature must be considered. By presented process, globular microstructure of the weld zone can be achieved. Moreover the near weld zone would have the globular structure due to semisolid holding. A gas heating system was designed to heat up the nitrogen gas to desired temperature accurately. A heating element was embedded in a castable ceramic block while a stream of gas could pass closely around the hot element length.... 

The mechanical properties of Mg-4wt.% Zn alloy single crystals along the [0001] orientation were measured through micropillar compression at 23 °C and 100 °C. Basal slip was dominant in the solution treated alloy, while pyramidal slip occurred in the precipitation hardened alloy. Pyramidal dislocations pass the precipitates by forming Orowan loops, leading to homogeneous deformation and to a strong hardening. The predictions of the yield stress based on the Orowan model were in reasonable agreement with the experimental data. The presence of rod-shape precipitates perpendicular to the basal plane leads to a strong reduction in the plastic anisotropy of Mg. © 2020 Elsevier B.V  

The mechanical properties of Mg-4wt.% Zn alloy single crystals along the [0001] orientation were measured through micropillar compression at 23 °C and 100 °C. Basal slip was dominant in the solution treated alloy, while pyramidal slip occurred in the precipitation hardened alloy. Pyramidal dislocations pass the precipitates by forming Orowan loops, leading to homogeneous deformation and to a strong hardening. The predictions of the yield stress based on the Orowan model were in reasonable agreement with the experimental data. The presence of rod-shape precipitates perpendicular to the basal plane leads to a strong reduction in the plastic anisotropy of Mg. © 2020 Elsevier B.V  

Recently, considerable attentions have been paid to alloy Mg-4Zn-0.2Ca for biomedical applications due to its suitable biocompatibility and acceptable mechanical properties. In this work, the effects of the addition of different amounts of Al on microstructure, mechanical properties, degradation behavior, and biocompatibility of this alloy were investigated. The corrosion behaviors of the alloys were investigated through polarization tests, chronoamperometry analysis, immersion tests, and EIS experiments. The mechanical properties were analyzed by using tensile tests and compression tests. The results showed that the addition of Al up to 3 wt.% considerably modifies the degradation behaviors... 

The corrosion behavior of different grades of commercial aluminum such as AA1040, AA5083, AA6060 and AA7075 in ZnO-containing 4 M NaOH has been determined by using open circuit potential-time measurements (OCP), galvanostatic and potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results of scanning electron microscopy (SEM) and energy dispersive analysis of X-ray (EDAX) reveal that ZnO produces the inhibition effect by the formation of a zinc-containing deposit layer on the surface of aluminum electrodes. Although the influence of zincating on the performance of aluminum alloys and considering the amount of alloying elements such as zinc, magnesium and... 

The non-isothermal aging behaviour of a newly developed Al–Zn–Mg–Cu alloy containing 17 wt-% Zn was investigated. Hardness and shear punch tests demonstrated that during non-isothermal aging, the mechanical properties of the alloy first increased and then decreased. The best properties were obtained in a sample which was non-isothermally aged upto 250°C with heating rate of 20°C min−1, due to the presence of η′/η (MgZn2) phases. This was confirmed by differential scanning calorimetery. After homogenisation, residual eutectic phases remained at triple junctions or in a spherical form. During aging, these phases transformed into rodlike S (Al2CuMg)-phase at 400°C, with sizes ranging from 50 to... 

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the deposition current density. The corrosion resistance of the deposits was studied and compared with that of monolayers of Ni-P and Zn-Ni alloys via Tafel polarization, EIS and salt spray tests. Characterization of corrosion products by means of EDS and XRD revealed more details from the corrosion mechanism of the monolayers and multilayers. The corrosion current density of Ni-P/Zn-Ni CMMCs were around one tenth of Zn-Ni monolayer. The CMMC with incomplete layers performed lower polarization resistance and higher corrosion current density compared to the CMMC with... 

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the cathodic current density. The composition, surface morphology, roughness, layers growth pattern as well as the phase structure of deposits were extensively studied via SEM, EDS, AFM and XRD analysis. Effects of bath ingredients on the electrodeposition behavior were analyzed through cathodic linear sweep voltammetry. Although the concentration of Zn2+ in bath was 13 times higher than Ni2+, the Zn-Ni deposition potential was much nearer to Ni deposition potential rather than that of Zn. Addition of NaH2PO2 to the Ni deposition bath considerably raised the current... 

We used first principles calculations based on density functional theory with generalized gradient approximation to investigate and compare the structural, electronic and optical properties of two photoanode materials, ZnV2O6 and Zn2V2O7, for use in photocatalytic water splitting. After geometry optimization, the calculated structural parameters evince a satisfactory agreement with the reported experimental results indicating that the used method and conditions are suitable. The electronic structures demonstrate that both photocatalysts possess favorable band gaps (2.31 and 2.52 eV) and appropriate band edge positions for oxygen evolution reaction under solar radiation. The relatively light... 

The non-isothermal aging behaviour of a newly developed Al–Zn–Mg–Cu alloy containing 17 wt-% Zn was investigated. Hardness and shear punch tests demonstrated that during non-isothermal aging, the mechanical properties of the alloy first increased and then decreased. The best properties were obtained in a sample which was non-isothermally aged upto 250°C with heating rate of 20°C min−1, due to the presence of η′/η (MgZn2) phases. This was confirmed by differential scanning calorimetery. After homogenisation, residual eutectic phases remained at triple junctions or in a spherical form. During aging, these phases transformed into rodlike S (Al2CuMg)-phase at 400°C, with sizes ranging from 50 to... 

In this study, nanostructured biodegradable pure Zn, Zn-4 wt. % Mn and Zn-24 wt % Mn alloys were produced by 20 h mechanical alloying and consequent cold pressing and sintering. Structural evolutions were investigated using the X-ray diffraction technique. Also, the microstructure was characterized by scanning electron microscopy. The effects of alloy composition on density, mechanical properties, corrosion behavior in Hank's solution, cell viability and cell attachment were investigated. Crystallite size of the synthesized alloys after 20 h of milling reached to less than 40 nm and remained less than 80 nm after consolidation and sintering for 1 h. Alloys contain MnZn13 as second phase... 

Al-Zn-Mg-Cu alloys (7xxx series Al alloys) are extensively used for their superior mechanical and corrosion performance. These properties are microstructure-sensitive and highly dependent on the formation, growth and coarsening of precipitates. To date, a wide variety of ageing procedures have been developed to tailor the evolved microstructures so as to yield a good combination of mechanical capacity and corrosion resistance of 7xxx series Al alloys. Among these methods, isothermal ageing, multi-stage ageing, non-isothermal ageing, retrogression and re-ageing (RRA), and stress ageing (i.e. creep ageing) are the most significant. In the present review, all of these approaches are... 

During the recent years, some Mg based alloys have extensively been considered as a new generation of degradable and absorbable bio-medical materials. In this work, the Mg–2Zn–1Gd–1Ca (wt%) alloy as a new metallic bio-material was produced by the casting process followed by the heat treatment. The samples of the alloy were solution treated at temperatures of 500, 550, and 600 °C and then quench aged at temperatures of 125, 150, and 175 °C. The results of SEM-EDS examinations indicated that the alloy microstructure consists of α-Mg matrix and the Ca2Mg6Zn3 and Mg3Gd2Zn3 secondary phases. With regard to the results of Vickers hardness test, the temperatures of 500 °C and 150 °C were selected... 

Mg-based metallic glasses are promising materials for biodegradable implants. Understanding atomistic mechanism behind glass formation in these glasses plays a critical role in developing them for future applications. In the present work, we perform a set of molecular dynamics simulations to study structural origin behind glass form ability of Mg-based Mg-Zn metallic glasses at a wide range of compositions. Pair distribution function, Voronoi tessellation and dynamical analysis were adopted to characterize local structures in these glasses. Structural analysis was performed considering both topological and chemical short-range orders. It was found that structure of Mg-Zn metallic glasses... 

This research aimed to prepare a recoverable sonophotocatalyst, in which microfibrillated carboxymethyl cellulose (MFC) acted as the Zn-Cu-Mg-mixed metal hydroxide/graphitic carbon nitride (MMH/g-C3N4) carrier. The characteristics of bare and composite sonophotocatalysts were analyzed by the XRD, FT-IR, BET, DRS, PL and FE-SEM equipped with the EDX mapping. The performance of prepared composites (MMH/g-C3N4@MFC) with various weight ratios of the MMH/g-C3N4 was studied for the sonophotocatalytic degradation of sulfadiazine (SDZ) as the model emerging contaminant. 93% of SDZ was degraded using the most effective catalyst (MMH/g-C3N4@MFC3) with 15% weight ratio of the MMH/g-C3N4 under the... 

Abstract: Further to traditional corrosion monitoring techniques for rated deteriorations, nowadays modern electrochemical monitoring methods are promising for the control of non-rated damage mechanisms. Considering carbon steel as the most commonly used alloy in the oil and gas industry, there are special grades under NACE MR0175 standard which are immune to sour corrosion. However, according to the industry reports, their immunity can be terminated by upset conditions or on site repairs. This issue will impose either a high operational risk or exorbitant maintenance and inspection costs. Hence, in this paper, a new monitoring technology framework is discussed to lessen a catastrophic... 

In this research, the ZnOG hybrid thin film was produced via solgel method. The surface morphology, band gap and photoactive properties of the films were studied by means of SEM, UV–Vis and photoluminescence analysis. In addition, the ability of the thin film in photocathodic protection of carbon steel (CS) and 304 stainless steel in 3.5 wt.% NaCl and Na2S solutions under dark and UV illumination was investigated by polarization test as well as OCP and current measurements during coupling of steels with ZnOG photoanode. The mix band gap is reduced to the orders of 1.17 eV through hybridization of ZnO with graphene oxide. In both NaCl and Na2S solutions, the ZnOG thin film could effectively... 

Magnesium alloys provide critical opportunities for energy and lightweight-materials challenges. The alloy design approach based on utilizing the second phase strengthening mechanism plays an essential role in producing low-density high strength Mg-based alloys. However, the second phase in the microstructure (e.g., Mg17Al12 phase in Mg–Al–Zn alloys) can deleteriously affect the weldability of the metallic materials by promoting the liquation and liquation cracking during fusion welding. The lack of sufficient weldability of Mg-based alloys is a crucial barrier to their potential use in safety-critical applications. In this paper, it is shown that the severe plastic deformation induced by... 

AZ91 alloy, the most widely used Mg casting alloy, exhibits low strength/ductility and weak energy absorption, which is a function of its large grain size and the presence of a coarse and continuous network of β-Mg17Al12 intermetallic compounds. This work demonstrated that friction stir processing (FSP) enables enhancement of strength and energy absorption capability of AZ91 alloy. The influence of FSP treatment on various potential strengthening mechanisms, including grain boundary, solid solution, and sub-micron particle strengthening mechanisms, was studied. It is identified that the grain boundary strengthening plays a significant contribution to the strength of the FSP treated AZ91. FSP...