The effects of bath composition and deposition variables on the electrodeposition of Zn–Ni–P alloys were studied in order to develop a single bath for deposition of Ni–P/Zn–Ni compositionally modulated multilayer coatings (CMMCs). The basis for development of the bath was a large increase in the Ni deposition rate compared to that of Zn at low deposition overpotentials combined with the impossibility of codeposition of Zn with P. EDS analysis demonstrated that the deposits obtained from the Zn–Ni–P bath at low overpotentials were practically all Ni–P, while the alloy deposited at high overpotentials was mainly Zn–Ni with around 3.2 wt% P content. © 2017 Elsevier B.V  

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the deposition current density. The corrosion resistance of the deposits was studied and compared with that of monolayers of Ni-P and Zn-Ni alloys via Tafel polarization, EIS and salt spray tests. Characterization of corrosion products by means of EDS and XRD revealed more details from the corrosion mechanism of the monolayers and multilayers. The corrosion current density of Ni-P/Zn-Ni CMMCs were around one tenth of Zn-Ni monolayer. The CMMC with incomplete layers performed lower polarization resistance and higher corrosion current density compared to the CMMC with... 

The Ni-P/Zn-Ni compositionally modulated multilayer coatings CMMCs were electrodeposited from a single bath by switching the cathodic current density. The composition, surface morphology, roughness, layers growth pattern as well as the phase structure of deposits were extensively studied via SEM, EDS, AFM and XRD analysis. Effects of bath ingredients on the electrodeposition behavior were analyzed through cathodic linear sweep voltammetry. Although the concentration of Zn2+ in bath was 13 times higher than Ni2+, the Zn-Ni deposition potential was much nearer to Ni deposition potential rather than that of Zn. Addition of NaH2PO2 to the Ni deposition bath considerably raised the current...