The fabrication of strong photocatalysts applied to the degradation of organic pollutants is necessary in environmental applications. In a single-stage method, acetate precursor and poly vinyl pyrolydine are used to produce ZnO nanostructures with various morphologies in annealing temperatures ranging from 300 to 900 °C. The physical properties of the prepared nanostructures were characterized by SEM, TEM, XRD, BET, DRS, CHN analysis and PL spectroscopy. The SEM images exhibit a variety of the as-prepared hexagonal zinc oxides including wires, rods, particles and porous network of welded particles of ZnO nanoparticles. The results of the photocatalytic degradation of methylene blue as an... 

Annealed and wrought AA5052 aluminum alloy was subjected to friction stir processing (FSP) without and with 3 vol pct TiO2 nanoparticles. Microstructural studies by electron backscattered diffraction and transmission electron microscopy showed the formation of an ultra-fine-grained structure with fine distribution of TiO2 nanoparticles in the metal matrix. Nanometric Al3Ti and MgO particles were also observed, revealing in-situ solid-state reactions between Al and Mg with TiO2. Tensile testing at different strain rates determined that FSP decreased the strain rate sensitivity and work hardening of annealed Al-Mg alloy without and with TiO2 nanoparticles, while opposite results were obtained... 

Abstract: Photocatalysis using semiconductors has emerged as a promising wastewater treatment process to overcome the major challenges faced by conventional technologies. The advantages of ZnO nanomaterials over other semiconductors, and their structure-dependent properties, make them important building blocks in nanotechnology as multifunctional materials. Moreover, it has been confirmed that ZnO nanomaterials can exhibit high performance in photodegradation of organic dyes for treatment of industrial effluent. The wurtzite structure of ZnO contains polar and nonpolar planes; the low surface energy and thermodynamic stability of the nonpolar planes enable formation of one-dimensional (1D)... 

The fabrication of strong photocatalysts applied to the degradation of organic pollutants is necessary in environmental applications. In a single-stage method, acetate precursor and poly vinyl pyrolydine are used to produce ZnO nanostructures with various morphologies in annealing temperatures ranging from 300 °C to 900 oC. The physical properties of the prepared nanostructures were characterized by SEM, XRD and PL spectroscopy. The SEM images exhibit a variety of the as-prepared hexagonal zinc oxides including wires, rods, particles and porous network of welded particles of ZnO nanoparticles. The results of the photocatalytic degradation of methylene blue as an organic dye in aqueous... 

Graphene oxide (GO) sheets with a low concentration (∼1 wt%) were deposited on surface of hydrothermally synthesized ZnO nanorod films. The deposited films were heat treated at 450 °C in order to achieve suitable GO/ZnO hybrid thin films for photocatalytic purposes. The photocatalytic activity of the nanocomposite films was investigated based on degradation of methylene blue (MB) dye which is a typical pollutant model. The GO/ZnO hybrid thin films could degrade higher MB (∼90%) than the bare ZnO nanorods (which showed only ∼75% degradation) after 450 min UV irradiation. A further significant improvement (resulting in a nearly complete degradation of MB) was achieved by exposing the GO/ZnO... 

Uniform layers of ZnO nanostructures were formed on quartz and alumina substrates through a simple vapor phase transport (VPT) method without any catalyst or buffer layer by making proper growth conditions. The effect of substrate on morphology, crystalline structure and photoluminescence spectra has been investigated. Scanning electron microscopy images revealed that morphlogical grwoth depends on used substrate, aligned rods with flower-like bundels and entangled rods are vertically aligned rods on the quartz and alumina substrates, respectively. X-ray diffraction studies showed that grown films on the quartz substrates possess stronger c-axis orientation compared to those on the alumina... 

The cauliflower like ZnO nanostructures are grown on ZnO nanorods using spray pyrolysis method. First, ZnO nanorod arrays are grown on p-type silicon substrate without catalyst by chemical vapor transport and condensation method in a horizontal tube furnace. Afterwards, the cauliflower like ZnO nanostructures is deposited on top of the ZnO nanorod array. The PL spectra of cauliflower like ZnO nanostructures consist of UV emission bands around 387 nm and a visible emission at ∼440 nm. The current-voltage (I-V) measurement under dark and UV illumination condition are performed to study photodetection of the cauliflower like ZnO-ZnO nanorod/p-Si heterostructure. The experimental data of dark... 

In this study, two different chemical solution methods were used to synthesize Zinc oxide nanostructures via a simple and fast microwave assisted method. Afterwards, the photocatalytic performances of the produced ZnO powders were investigated using methylene blue (MB) photodegradation with UV lamp irradiation. The obtained ZnO nanostructures showed spherical and flower-like morphologies. The average crystallite size of the flower-like and spherical nanostructures were determined to be about 55 nm and 28 nm, respectively. X-ray diffraction (XRD), scanning electronic microscopy (SEM), Brunauer-Emmett-Teller (BET), room temperature photoluminescence (RT-PL) and UV-vis analysis were used for... 

ZnO nano-architectures were produced with the aid of a fast, simple and low cost microwave-assisted synthesis method. Solid semispherical ZnO nanoparticles on the order of 600 nm in diameter along with rice-like ZnO nanorods 95 nm thick were produced from butanol, triethanolamine (TEA), and zinc acetate dihydrate. Solid spherical ZnO nano-architectures with an average diameter of 250 nm were produced from the same starting materials in addition to NaOH. X-ray diffraction, scanning electron microscopy, and transmission electron microscopy were used to characterize the ZnO nano-architectures as well as the precursor. This method is cheap, fast and simple; capable of producing large quantities... 

ZnO nanostructures were synthesized through arc discharge of zinc electrodes in deionized (DI) water. X-ray diffraction (XRD) analysis of the prepared nanostructures indicates formation of crystalline ZnO of hexagonal lattice structures. Transmission electron microscopy (TEM) images illustrate rod-like as well as semi spherical ZnO nanoparticles with 15-20 nm diameter range, which were formed during the discharge process with 5 A arc current. The average particle size was found to increase with the increasing arc current. X-ray photoelectron spectroscopy (XPS) analysis confirms formation of ZnO at the surface of the nanoparticles. Surface area of the sample prepared at 5 A arc current,... 

Through a fast, simple, low cost, surfactant-free and convenient microwave-assisted route, narcis-like ZnO nanostructures (10-15 nm size) with flower diameters in the range of 1-2.5 μm were synthesized. X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR) spectroscopy and room temperature photoluminescence (PL) measurements were used to characterize the produced ZnO nanostructures. The principle raw materials - ammonium hydroxide (NH4OH) and zinc acetate dihydrate [Zn(CH3COO)2·2H2O] - were both inexpensive. The method was fast, simple and surfactant-free capable of producing larger quantities of zinc oxide... 

ZnO nanostructures in the shape of particle, rods, flower-like and micro-sphere were synthesized via facile hydrothermal methods and the effect of morphology on the decolorization of CI Acid Red 27 solution under direct irradiation of sunlight was investigated. XRD patterns showed that the synthesized nanostructures have Wurtzite-type hexagonal structure with high crystallinity and crystallite size in the range of 67-100 nm. UV-vis absorption spectra indicated that the ZnO nanorods have higher visible light harvesting as compared to the other morphologies. The decolorization obeys the first order kinetics rate with the kinetics constant of 4.5-19.5 × 10-3 min-1 dependent on the ZnO... 

ZnO tetrapods and rods were grown on silicon and thermally oxidized porous silicon substrates with and without Au catalyst layer by carbothermal reduction of ZnO powder through chemical vapor transport and condensation method (CVTC). Porous silicon was fabricated by electrochemical etching of silicon in HF solution. The effect of substrates on morphology, structure and photoluminescence spectra of ZnO nanostructures has been studied. The texture coefficient (TC) of each sample was calculated from XRD data that demonstrated random orientation of ZnO nanostructures on the oxidized porous silicon substrate. Moreover, TC indicates the effect of Au catalyst layer on formation of more highly... 

The ZnO nanowires have been synthesized using vapor-liquid-solid (VLS) process on Au catalyst thin film deposited on different substrates including Si(1 0 0), epi-Si(1 0 0), quartz and alumina. The influence of surface roughness of different substrates and two different environments (Ar + H2 and N2) on formation of ZnO nanostructures was investigated. According to AFM observations, the degree of surface roughness of the different substrates is an important factor to form Au islands for growing ZnO nanostructures (nanowires and nanobelts) with different diameters and lengths. Si substrate (without epi-taxy layer) was found that is the best substrate among Si (with epi-taxy layer), alumina and... 

Arrays of ZnO nanorods were synthesized on ZnO seed layer/glass substrates by a hydrothermal method at a low temperature of 70 °C. The effect of pH > 7 of the hydrated zinc nitrate-NaOH precursor on the morphology and topography (e.g. size, surface area and roughness), the optical characteristics (e.g. optical transmission and band-gap energy), hydrophilicity and antibacterial activity of the grown ZnO nanostructure and nanorod coatings were investigated. For pH = 11.33 of the precursor (NaOH concentration of 0.10M), a fast growth of ZnO nanorods on the seed layer (length of ∼1 νm in 1.5 h) was observed. The fast growth of the ZnO nanorods resulted in a significant reduction in the optical...