Hydrolyzed Protein-Based Highly Porous Hydrogels: Synthesis and Characteristics, Ph.D. Dissertation Sharif University of Technology ; Pourjavadi, Ali (Supervisor)
Abstract
This thesis focuses on the preparation and super-swelling behavior of four highly porous hydrogels: 1. Firstly, we have developed a collagen-based highly porous hydrogel by neutralizing the grafted poly(acrylamide-co-acrylic acid) after gel formation. Systematically, the certain variables of the graft copolymerization were optimized to achieve maximum swelling capacity. Morphology of the samples was examined by scanning electron microscopy (SEM) and was shown the pores were induced into the hydrogel by water evaporation resulting from neutralization process. The absorbency under load (AUL) and centrifuge retention capacity (CRC) were measured. The synthesized hydrogel exhibited a...
Cataloging briefHydrolyzed Protein-Based Highly Porous Hydrogels: Synthesis and Characteristics, Ph.D. Dissertation Sharif University of Technology ; Pourjavadi, Ali (Supervisor)
Abstract
This thesis focuses on the preparation and super-swelling behavior of four highly porous hydrogels: 1. Firstly, we have developed a collagen-based highly porous hydrogel by neutralizing the grafted poly(acrylamide-co-acrylic acid) after gel formation. Systematically, the certain variables of the graft copolymerization were optimized to achieve maximum swelling capacity. Morphology of the samples was examined by scanning electron microscopy (SEM) and was shown the pores were induced into the hydrogel by water evaporation resulting from neutralization process. The absorbency under load (AUL) and centrifuge retention capacity (CRC) were measured. The synthesized hydrogel exhibited a...
Find in contentBookmark |
|