The Corrosion Behavior of Sulfur Concrete in Persian Gulf Sea Water, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
In this project sulfur concretes were prepared. The optimum of casting temperature, weight percent of sulfur cement and weight percent of filler were analyzed, so that better corrosion resistance could be found. It is observed, the optimum sulfur is 15% for sulfur concrete samples with 21% sulfur cement; the optimum filler is 10-15% with 18% sulfur cement and finally the optimum filler is 10% for concrete samples with 15% sulfur cement. The casting temperature for concrete with 15-21% sulfur cement is in the interval of 127-150°C could be achieved. By applying the relation between the optimum filler percent and the content of sulfur cement and choosing a suitable temperature for casting...
Cataloging briefThe Corrosion Behavior of Sulfur Concrete in Persian Gulf Sea Water, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
In this project sulfur concretes were prepared. The optimum of casting temperature, weight percent of sulfur cement and weight percent of filler were analyzed, so that better corrosion resistance could be found. It is observed, the optimum sulfur is 15% for sulfur concrete samples with 21% sulfur cement; the optimum filler is 10-15% with 18% sulfur cement and finally the optimum filler is 10% for concrete samples with 15% sulfur cement. The casting temperature for concrete with 15-21% sulfur cement is in the interval of 127-150°C could be achieved. By applying the relation between the optimum filler percent and the content of sulfur cement and choosing a suitable temperature for casting...
Find in contentBookmark |
|