Electrodeposition of the Ni-P by Pulse Plating, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
Ni-P alloy coatings were electrodeposited using pulse current in a watt type bath in various conditions. The influences of different parameters were investigated and optimized for the highest amount of coating hardness using the Design Of Experiment (DOE) method. The optimized deposition parameters were current density 23.7 A/dm2, duty cycle 75%, frequency equal to 188 Hz, temperature equal to 70ºC and 17.5 gr/l of H3PO3. The DOE prediction of hardness for the optimized coatings was between 700 and 750 the achieved micro-hardness was about 725.8 HV. It was obtained that an increase of the current density will improve micro-hardness, decreases P content and increase deposition rate. Also, the...
Cataloging briefElectrodeposition of the Ni-P by Pulse Plating, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
Ni-P alloy coatings were electrodeposited using pulse current in a watt type bath in various conditions. The influences of different parameters were investigated and optimized for the highest amount of coating hardness using the Design Of Experiment (DOE) method. The optimized deposition parameters were current density 23.7 A/dm2, duty cycle 75%, frequency equal to 188 Hz, temperature equal to 70ºC and 17.5 gr/l of H3PO3. The DOE prediction of hardness for the optimized coatings was between 700 and 750 the achieved micro-hardness was about 725.8 HV. It was obtained that an increase of the current density will improve micro-hardness, decreases P content and increase deposition rate. Also, the...
Find in contentBookmark |
|