Fabrication of a Sensor, Based on TiO2 Nanotubes Modified with Metal Nanoparticles and Carbon and its Application for Detection of Dopamine in Presence of Uric Acid and Ascorbic Acid, Ph.D. Dissertation Sharif University of Technology ; Askari, Masoud (Supervisor) ; Dolati, Abolghasem (Supervisor)
Abstract
The present work describes sensing application of modified TiO2 nanotubes towards detection of dopamine. The TiO2 nanotubes electrode was prepared using anodizing method at different conditions, among which NaF/ NaHSO4 solution and voltage of 15 V was chosen as the optimum condition. In order to improve the performance, surface modification with metal nanoparticles (Pd, Pt and Au) and carbon is required using “pulse electrodeposition” and “decomposition of polyethylene glycol at 600 °C” respectively. Carbon was deposited by decomposition of polyethylene glycol in a tube furnace to improve the conductivity. In this regard two type of electrodes were proposed: Pd-Pt-Au-TiO2 and C-Ni(Pt)-TiO2....
Cataloging briefFabrication of a Sensor, Based on TiO2 Nanotubes Modified with Metal Nanoparticles and Carbon and its Application for Detection of Dopamine in Presence of Uric Acid and Ascorbic Acid, Ph.D. Dissertation Sharif University of Technology ; Askari, Masoud (Supervisor) ; Dolati, Abolghasem (Supervisor)
Abstract
The present work describes sensing application of modified TiO2 nanotubes towards detection of dopamine. The TiO2 nanotubes electrode was prepared using anodizing method at different conditions, among which NaF/ NaHSO4 solution and voltage of 15 V was chosen as the optimum condition. In order to improve the performance, surface modification with metal nanoparticles (Pd, Pt and Au) and carbon is required using “pulse electrodeposition” and “decomposition of polyethylene glycol at 600 °C” respectively. Carbon was deposited by decomposition of polyethylene glycol in a tube furnace to improve the conductivity. In this regard two type of electrodes were proposed: Pd-Pt-Au-TiO2 and C-Ni(Pt)-TiO2....
Find in contentBookmark |
|