Investigation of Toughening Mechanisms in Al/Al3Ti In-Situ Hot Extruded Composites, M.Sc. Thesis Sharif University of Technology ; Madaah Hosseini, Hamid Reza (Supervisor)
Abstract
In this study in-situ Al/Al3Ti was fabricated by mechanical alloying, hot extrusion and subsequent heat treatment. First, initial pure powders of Al and Ti were mechanically alloyed with 5 weight percentages of Ti for 40 hours. The as-hot extruded samples containing 5 wt% of initial Ti particles, were exposed to heating at 600 oC for various time intervals up to 10 hours. Microstructure analysis by OM and SEM proved that in-situ Al3Ti phase was formed as a layer around Ti particles by solid reactive diffusion between Al and Ti particles. After 10 hours of heating, all the Ti particles were consumed and transformed to Al3Ti. Mechanical properties of samples were investigated by Brinell...
Cataloging briefInvestigation of Toughening Mechanisms in Al/Al3Ti In-Situ Hot Extruded Composites, M.Sc. Thesis Sharif University of Technology ; Madaah Hosseini, Hamid Reza (Supervisor)
Abstract
In this study in-situ Al/Al3Ti was fabricated by mechanical alloying, hot extrusion and subsequent heat treatment. First, initial pure powders of Al and Ti were mechanically alloyed with 5 weight percentages of Ti for 40 hours. The as-hot extruded samples containing 5 wt% of initial Ti particles, were exposed to heating at 600 oC for various time intervals up to 10 hours. Microstructure analysis by OM and SEM proved that in-situ Al3Ti phase was formed as a layer around Ti particles by solid reactive diffusion between Al and Ti particles. After 10 hours of heating, all the Ti particles were consumed and transformed to Al3Ti. Mechanical properties of samples were investigated by Brinell...
Find in contentBookmark |
|