Design and Fabrication of Conductive Polymeric Nanocomposite Scaffolds for Nerve Tissue Engineering, Ph.D. Dissertation Sharif University of Technology ; Ramezani Saadat, Ahmad (Supervisor)
Abstract
In the current study, design, fabrication, and characterization of a novel conductive nanocomposite scaffold for nerve tissue engineering applications is reported. For this purpose, the highly conductive polyaniline/graphene nanocomposite (PAG) was synthesized via emulsion polymerization, used for fabrication of conductive chitosan/gelatin/PAG scaffolds, and the effect of PAG amount on the various properties of scaffolds were investigated. The synthesized graphene, polyaniline, and PAG were characterized and the obtained results revealed that partially exfoliated graphene nanosheets and highly conductive PAG with a conductivity of about 12 S.cm-1 and 7 S.cm-1, respectively were obtained. The...
Cataloging briefDesign and Fabrication of Conductive Polymeric Nanocomposite Scaffolds for Nerve Tissue Engineering, Ph.D. Dissertation Sharif University of Technology ; Ramezani Saadat, Ahmad (Supervisor)
Abstract
In the current study, design, fabrication, and characterization of a novel conductive nanocomposite scaffold for nerve tissue engineering applications is reported. For this purpose, the highly conductive polyaniline/graphene nanocomposite (PAG) was synthesized via emulsion polymerization, used for fabrication of conductive chitosan/gelatin/PAG scaffolds, and the effect of PAG amount on the various properties of scaffolds were investigated. The synthesized graphene, polyaniline, and PAG were characterized and the obtained results revealed that partially exfoliated graphene nanosheets and highly conductive PAG with a conductivity of about 12 S.cm-1 and 7 S.cm-1, respectively were obtained. The...
Find in contentBookmark |
|