Synthesis of Composite Coating with HA Nanoparticles on Ti by AC Plasma Electrolyte Oxidation, M.Sc. Thesis Sharif University of Technology ; Ghorbani, Mohammad (Supervisor)
Abstract
In this project, a ceramic biocompatible coating was applied on Titanium which is included Hydroxyapatite by AC Plasma Electrolyte Oxidation method. First, coating was performed in 5 different solutions and various duration in 500mA/Cm2 as a current density. Then, by microscopic and macroscopic images and size of porosity and also thickness of coat, 3 solutions were chosen for adding nanoparticles: Solution 1 which includes NaH2PO4 and Ca(CH3COO)2 , Solution 3 which includes Ca(CH3COO)2 and Na-Beta G and Solution 4 which includes Ca(H2PO4)2, HMP, NA2(EDTA) and Ca(CH3COO)2 . Also the time 10 minutes was chose as a appropriate time. The average of the porosities size in solution 1 was about...
Cataloging briefSynthesis of Composite Coating with HA Nanoparticles on Ti by AC Plasma Electrolyte Oxidation, M.Sc. Thesis Sharif University of Technology ; Ghorbani, Mohammad (Supervisor)
Abstract
In this project, a ceramic biocompatible coating was applied on Titanium which is included Hydroxyapatite by AC Plasma Electrolyte Oxidation method. First, coating was performed in 5 different solutions and various duration in 500mA/Cm2 as a current density. Then, by microscopic and macroscopic images and size of porosity and also thickness of coat, 3 solutions were chosen for adding nanoparticles: Solution 1 which includes NaH2PO4 and Ca(CH3COO)2 , Solution 3 which includes Ca(CH3COO)2 and Na-Beta G and Solution 4 which includes Ca(H2PO4)2, HMP, NA2(EDTA) and Ca(CH3COO)2 . Also the time 10 minutes was chose as a appropriate time. The average of the porosities size in solution 1 was about...
Find in contentBookmark |
|