Ni-doped TiO2 Photoanode Electrodes for Dye-sensitized Solar Cells Applications, M.Sc. Thesis Sharif University of Technology ; Mohammadi, Mohammad Reza (Supervisor)
Abstract
A new strategy for enhancing the efficiency of TiO2 dye sensitized solar cells (DSSCs) doped with Ni ions with different molar percentages (i.e., 0, 0.5, 1, 5 and 10 mol%) was reported. The samples were prepared by sol-gel route and characterized by means of XRD, DRS, UV-visible, FESEM and photovoltaic measurment techniques. It was found that Ni-doped TiO2 nanoparticles had a mixture of anatase, rutile and brookite crystal structures. Moreover, the band gap energy was decreased with increasing Ni molar ratio, The highest cell efficiency of 5.4% was achieved for 1mol% Ni-doped TiO2, being 42% greater than that of pure TiO2 nanoparticles
Cataloging briefNi-doped TiO2 Photoanode Electrodes for Dye-sensitized Solar Cells Applications, M.Sc. Thesis Sharif University of Technology ; Mohammadi, Mohammad Reza (Supervisor)
Abstract
A new strategy for enhancing the efficiency of TiO2 dye sensitized solar cells (DSSCs) doped with Ni ions with different molar percentages (i.e., 0, 0.5, 1, 5 and 10 mol%) was reported. The samples were prepared by sol-gel route and characterized by means of XRD, DRS, UV-visible, FESEM and photovoltaic measurment techniques. It was found that Ni-doped TiO2 nanoparticles had a mixture of anatase, rutile and brookite crystal structures. Moreover, the band gap energy was decreased with increasing Ni molar ratio, The highest cell efficiency of 5.4% was achieved for 1mol% Ni-doped TiO2, being 42% greater than that of pure TiO2 nanoparticles
Find in contentBookmark |
|