Synthesis and Microstructure of Multi Valent Heavily Doped TiO2 Ceramics, M.Sc. Thesis Sharif University of Technology ; Nemati, Ali (Supervisor)
Abstract
In this project, the nanostructured titanium oxide with heaily doping of oxides of cerium and tin was synthesized using the sol-gel process and its properties were studied. To synthesize TiO2, titanium tetraisopropoxide precursor was used. Cerium nitrate and aqueous tin chloride precursors were utilized for cerium and tin synthesis. Then, they were mixed with Titania precursor causing a severe doping. After that, a gel was produced and it was aged and eventually, it was dried and calcined. XRD and SEM were used to determine the phase and particle size SEM and XRD results showed that doping had great impact on TiO2 crystals. The approximate size of nanoparticles was calculated using...
Cataloging briefSynthesis and Microstructure of Multi Valent Heavily Doped TiO2 Ceramics, M.Sc. Thesis Sharif University of Technology ; Nemati, Ali (Supervisor)
Abstract
In this project, the nanostructured titanium oxide with heaily doping of oxides of cerium and tin was synthesized using the sol-gel process and its properties were studied. To synthesize TiO2, titanium tetraisopropoxide precursor was used. Cerium nitrate and aqueous tin chloride precursors were utilized for cerium and tin synthesis. Then, they were mixed with Titania precursor causing a severe doping. After that, a gel was produced and it was aged and eventually, it was dried and calcined. XRD and SEM were used to determine the phase and particle size SEM and XRD results showed that doping had great impact on TiO2 crystals. The approximate size of nanoparticles was calculated using...
Find in contentBookmark |
|