Electrochemical and Microstructural Analysis of Aging Mechanism of 18650 LiFePO4/Graphite Li-ion Batteries under Different C-Rate and Temperature Conditions, M.Sc. Thesis Sharif University of Technology ; Asgari, Sirous (Supervisor)
Abstract
In this study, the aging of the LiFePO4/graphite cell was investigated in two different types of 18650 Li-ion batteries during cycling at various C-rates (0.5, 1, 2, 3, 4C) and high temperature under long-term cycling. An amount of 20% Capacity loss was considered as the end of the cycling. Batteries with a capacity of 1500 mAh after this capacity drop, experience 60, 120, 1502, and 2155 cycles, at the rates of 4, 3, 2, and 1C , and batteries with capacity of 1400 mAh was also 60, 360, 1100, 1000, and 805 cycles at a rate of 0.5C. Capacity decrease of the cell is in linear relationship with cycle number and the slope of the capacity-fading line increases with elevating current rate. Aging...
Cataloging briefElectrochemical and Microstructural Analysis of Aging Mechanism of 18650 LiFePO4/Graphite Li-ion Batteries under Different C-Rate and Temperature Conditions, M.Sc. Thesis Sharif University of Technology ; Asgari, Sirous (Supervisor)
Abstract
In this study, the aging of the LiFePO4/graphite cell was investigated in two different types of 18650 Li-ion batteries during cycling at various C-rates (0.5, 1, 2, 3, 4C) and high temperature under long-term cycling. An amount of 20% Capacity loss was considered as the end of the cycling. Batteries with a capacity of 1500 mAh after this capacity drop, experience 60, 120, 1502, and 2155 cycles, at the rates of 4, 3, 2, and 1C , and batteries with capacity of 1400 mAh was also 60, 360, 1100, 1000, and 805 cycles at a rate of 0.5C. Capacity decrease of the cell is in linear relationship with cycle number and the slope of the capacity-fading line increases with elevating current rate. Aging...
Find in contentBookmark |
|