Coating Nano Composite HAp-Al2O3-TiO2 on Stainless Steel 316 by Sol-Gel Method, M.Sc. Thesis Sharif University of Technology ; Afshar, Abdollah (Supervisor)
Abstract
316L stainless steel is used in implants under load in orthopedics and dentistry due to its high strength and corrosion resistance. Therefore, to improve their biocompatibility properties, bioceramic coatings with more suitable biocompatibility properties are used. Therefore, in the present study, to improve the biocompatibility and corrosion properties on 316 L metal implants, HAp / TiO2 / Al2O3 nanocomposite coating was created using the cost-effective sol-gel method. Titanium + alumina by weight percentage in these coatings were 20, 30, and 40% by weight. In this study, FTIR, XRD, DSC / TG, FE-SEM EDS, DLS tests were performed to investigate the chemical bases in nanocomposites,...
Cataloging briefCoating Nano Composite HAp-Al2O3-TiO2 on Stainless Steel 316 by Sol-Gel Method, M.Sc. Thesis Sharif University of Technology ; Afshar, Abdollah (Supervisor)
Abstract
316L stainless steel is used in implants under load in orthopedics and dentistry due to its high strength and corrosion resistance. Therefore, to improve their biocompatibility properties, bioceramic coatings with more suitable biocompatibility properties are used. Therefore, in the present study, to improve the biocompatibility and corrosion properties on 316 L metal implants, HAp / TiO2 / Al2O3 nanocomposite coating was created using the cost-effective sol-gel method. Titanium + alumina by weight percentage in these coatings were 20, 30, and 40% by weight. In this study, FTIR, XRD, DSC / TG, FE-SEM EDS, DLS tests were performed to investigate the chemical bases in nanocomposites,...
Find in contentBookmark |
|