Evaluation the Effect of Oxidized Nano MoS2 on Epoxy Novolac Corrosion Resistance and Rheological Properties, M.Sc. Thesis Sharif University of Technology ; Ramezani Saadat Abadi, Ahmad (Supervisor) ; Mousavi, Abbas (Supervisor)
Abstract
This study investigated the effect of oxidized molybdenum disulfide (MoS2) nanosheets on the anti-corrosion and rheological properties of epoxy resin. Raw MoS2 sheets were obtained as layered nanosheets with a thickness of 50 to 100 nm using acid washing, oxidation, and heat shock methods. The use of nanoparticle characterization tests such as XRD, FT-IR, FE-SEM, EDS, and TGA supports this claim. Then, in the next step, epoxy coatings containing different percentages (0, 0.3, 0.5, 0.8, and 1.5 wt%) of MoS2 nanosheets were prepared with polyamide hardener to investigate the effect of adding nanosheets and the optimal percentage. The best effect on the corrosion properties of the coating in a...
Cataloging briefEvaluation the Effect of Oxidized Nano MoS2 on Epoxy Novolac Corrosion Resistance and Rheological Properties, M.Sc. Thesis Sharif University of Technology ; Ramezani Saadat Abadi, Ahmad (Supervisor) ; Mousavi, Abbas (Supervisor)
Abstract
This study investigated the effect of oxidized molybdenum disulfide (MoS2) nanosheets on the anti-corrosion and rheological properties of epoxy resin. Raw MoS2 sheets were obtained as layered nanosheets with a thickness of 50 to 100 nm using acid washing, oxidation, and heat shock methods. The use of nanoparticle characterization tests such as XRD, FT-IR, FE-SEM, EDS, and TGA supports this claim. Then, in the next step, epoxy coatings containing different percentages (0, 0.3, 0.5, 0.8, and 1.5 wt%) of MoS2 nanosheets were prepared with polyamide hardener to investigate the effect of adding nanosheets and the optimal percentage. The best effect on the corrosion properties of the coating in a...
Find in contentBookmark
|
|