Study of Temperature and Stress Effects on Phase Transformation in MP35N, M.Sc. Thesis Sharif University of Technology ; Asgari, Sirous (Supervisor)
Abstract
Many Investigations have been carried out on high work hardening, strengthening and secondary hardening of MP35N superalloy. In this study, behavior of MP35N under uniaxial hot compression at 600 °C with true strain of 0.05, 0.10, 0.16 and 0.22 was investigated. After calculating on stress- true strain curve, work hardening rate versus strain come out. Serrated flow has been seen in all mentioned strains. In TEM investigation on these samples, dislocations array with extended faults and micro twinning have been seen. According to Suzuki mechanism with solute partitioning and diffusion of solute, stacking fault extended. Uninterrupted separations and combinations of partial dislocations lead...
Cataloging briefStudy of Temperature and Stress Effects on Phase Transformation in MP35N, M.Sc. Thesis Sharif University of Technology ; Asgari, Sirous (Supervisor)
Abstract
Many Investigations have been carried out on high work hardening, strengthening and secondary hardening of MP35N superalloy. In this study, behavior of MP35N under uniaxial hot compression at 600 °C with true strain of 0.05, 0.10, 0.16 and 0.22 was investigated. After calculating on stress- true strain curve, work hardening rate versus strain come out. Serrated flow has been seen in all mentioned strains. In TEM investigation on these samples, dislocations array with extended faults and micro twinning have been seen. According to Suzuki mechanism with solute partitioning and diffusion of solute, stacking fault extended. Uninterrupted separations and combinations of partial dislocations lead...
Find in contentBookmark |
|