Improve the Structure of Membrane Bioreactor to Reduce Fouling for Industrial Waste Water Purification, M.Sc. Thesis Sharif University of Technology ; Seifkordi, Ali Akbar (Supervisor) ; Hemati, Mahmood (Co-Advisor)
Abstract
In the presence project by using of hydrophilic polymer, Cellulose acetate (CA), we tried to modify the membrane made of Polyvinylidine fluoride (PVDF). The membranes were made by phase inversion method. In five levels, at least 10% and at most 30%, CA was added to casting solution. The hydrophilicity of membranes’ surface and pore size was increased. The permeation of the neat membrane of PVDF was less than 10 , on the other hand the permeation of the membranes, which were made by adding CA, was increased up to 500 . The increment of CA more than 20% reduced the porosity of membrane. In the next step to reduce the irreversibility fouling tried to reduce the pore size by adding some...
Cataloging briefImprove the Structure of Membrane Bioreactor to Reduce Fouling for Industrial Waste Water Purification, M.Sc. Thesis Sharif University of Technology ; Seifkordi, Ali Akbar (Supervisor) ; Hemati, Mahmood (Co-Advisor)
Abstract
In the presence project by using of hydrophilic polymer, Cellulose acetate (CA), we tried to modify the membrane made of Polyvinylidine fluoride (PVDF). The membranes were made by phase inversion method. In five levels, at least 10% and at most 30%, CA was added to casting solution. The hydrophilicity of membranes’ surface and pore size was increased. The permeation of the neat membrane of PVDF was less than 10 , on the other hand the permeation of the membranes, which were made by adding CA, was increased up to 500 . The increment of CA more than 20% reduced the porosity of membrane. In the next step to reduce the irreversibility fouling tried to reduce the pore size by adding some...
Find in contentBookmark |
|