A Study on Properties of Composite Coating with Al2O3 Base Prepared by Hard Anodizing with ZrO2 Nanoparticles, M.Sc. Thesis Sharif University of Technology ; Afshar, Abdollah (Supervisor)
Abstract
In this study anodized none composite and composite film containing ZrO2 nanoparticles were prepared on 1050 Al Alloy using hard anodizing method in sulfuric and oxalic acid mixed solution by pulse Currents. The microstructure and properties of the film were studied by field emission scanning electron microscopy with EDS analyzer and XRD diffraction and friction wear test were performed to evaluate the mechanical properties of coating . Results indicate that the composite film with ZrO2 nanoparticles have reduced friction coefficient with high micro hardness friction coefficient of composite film can be small as 0.16 which is much smaller than that 0.39 of none composite film. Micro hardness...
Cataloging briefA Study on Properties of Composite Coating with Al2O3 Base Prepared by Hard Anodizing with ZrO2 Nanoparticles, M.Sc. Thesis Sharif University of Technology ; Afshar, Abdollah (Supervisor)
Abstract
In this study anodized none composite and composite film containing ZrO2 nanoparticles were prepared on 1050 Al Alloy using hard anodizing method in sulfuric and oxalic acid mixed solution by pulse Currents. The microstructure and properties of the film were studied by field emission scanning electron microscopy with EDS analyzer and XRD diffraction and friction wear test were performed to evaluate the mechanical properties of coating . Results indicate that the composite film with ZrO2 nanoparticles have reduced friction coefficient with high micro hardness friction coefficient of composite film can be small as 0.16 which is much smaller than that 0.39 of none composite film. Micro hardness...
Find in contentBookmark |
![]() |
|