Fatigue properties of temperature gradient transient liquid phase diffusion bonded Al7075-T6 alloy

Seyyed Afghahi, S. S ; Sharif University of Technology | 2015

700 Viewed
  1. Type of Document: Article
  2. DOI: 10.1016/S1003-6326(15)63700-1
  3. Publisher: Nonferrous Metals Society of China , 2015
  4. Abstract:
  5. Abstract Fatigue properties of Al7075-T6 alloy joined by temperature gradient transient liquid phase (TGTLP) diffusion bonding using liquid gallium interlayer was investigated. The fatigue specimen was jointed at 460 °C under 10 MPa pressure for 10 min. The TLP bonded samples were homogenized at 465 °C for 2 h and then T6-heat treated. The fatigue life of Al7075-T6 alloy was determined as 107 cycles under 90 MPa while the fatigue life of TLP bonded sample under this stress amplitude was 1.2×106 cycles, which is about 10% of the total Al7075 alloy fatigue life. The fatigue fracture surfaces of Al7075 sample and TGTLP bonded sample were studied using scanning electron microscope to characterize the nucleation sites and crack growth stages in both samples
  6. Keywords:
  7. Al7075 alloy ; Fatigue ; Alloys ; Crack propagation ; Fatigue of materials ; Gallium ; Gallium alloys ; Scanning electron microscopy ; Temperature ; Thermal gradients ; Fatigue fracture surfaces ; Fatigue properties ; Fatigue specimen ; Growth stages ; Liquid gallium ; Nucleation sites ; Stress amplitudes ; Transient liquid phase ; Liquids
  8. Source: Transactions of Nonferrous Metals Society of China (English Edition) ; Volume 25, Issue 4 , April , 2015 , Pages 1073-1079 ; 10036326 (ISSN)
  9. URL: http://www.sciencedirect.com/science/article/pii/S1003632615637001