Corrosion Behavior of Hydrophobic Silane Coating Prepared by Sol–gel Method on Carbon Steel, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
This project aims to study corrosion protection performance of silane coating based on tetraethylorthosilicate (TEOS), (3-Mercaptopropyl) trimethoxysilane (MPTS) and Hexamethyldisilazane (HMDS) on carbon steel substrate. Water contact angle (WCA) were measured to study hydrophobicity. The water contact angle increased from 60 degrees in carbon steel to 134.8 degrees in the sample containing 0.35 MPTS and 1.25 HMDS. Surface morphology was studied using Field emission scanning electron microscopy (FESEM) and chemical analysis was conducted using Fourier Transform Infrared Spectroscopy (FTIR). Corrosion resistance was studied by means of Electrochemical Impedance Spectroscopy (EIS) and tafel...
Cataloging briefCorrosion Behavior of Hydrophobic Silane Coating Prepared by Sol–gel Method on Carbon Steel, M.Sc. Thesis Sharif University of Technology ; Dolati, Abolghasem (Supervisor)
Abstract
This project aims to study corrosion protection performance of silane coating based on tetraethylorthosilicate (TEOS), (3-Mercaptopropyl) trimethoxysilane (MPTS) and Hexamethyldisilazane (HMDS) on carbon steel substrate. Water contact angle (WCA) were measured to study hydrophobicity. The water contact angle increased from 60 degrees in carbon steel to 134.8 degrees in the sample containing 0.35 MPTS and 1.25 HMDS. Surface morphology was studied using Field emission scanning electron microscopy (FESEM) and chemical analysis was conducted using Fourier Transform Infrared Spectroscopy (FTIR). Corrosion resistance was studied by means of Electrochemical Impedance Spectroscopy (EIS) and tafel...
Find in contentBookmark |
|
|