Self-compacting concrete (SCC) is a highly-workable concrete that without any vibration or impact and under its own weight fills the formwork, and it also passes easily through small spaces between rebars. In this paper, the effect of steel fibers on rheological properties, compressive strength, splitting tensile strength, flexural strength, and flexural toughness of SCC specimens, using four different steel fiber volume fractions (0.5%, 1%, 1.5%, and 2%), were investigated. Two mix designs with strengths of 40 MPa (medium strength) and 60 MPa (high strength) were considered. Rheological properties were determined through slump flow time and diameter, L-box, and V-funnel flow time tests.... 

In this work, cristobalite crystallization and its effects on mechanical and chemical behaviour of injection moulded silica-based ceramic cores were investigated. In order to simulate casting process condition, the sintered samples at 1220 °C were also heated up to 1430 °C. Flexural strength test was carried out on both sintered and heat treated samples. Chemical resistance of the cores was evaluated by leaching the samples inside 43. wt% KOH solution at its boiling point. Phase evolution and microstructure were investigated by thermal analyses (DTA and DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and optical microscopy (OM). Results showed that cristobalite was... 

Addition of fine zirconia particles in the alumina matrix in order to produce ZTA composite is a well-known method for improving the mechanical properties of alumina ceramics such as flexural strength and fracture toughness. Increasing homogeneity and reducing alumina grain size are two key factors for achieving proper mechanical properties in this ceramic matrix composite. In this work two batches of ZTA powder precursor were prepared through mixing of alumina and zirconia by ball milling and in situ synthesis of ZTA composite via solution combustion method. The bending strength testing samples were fabricated through gel-casting process. The effects of different powder processing methods... 

This paper presents the results of an experimental study on the flexural behavior of ten 10 × 15 × 120 (cm) steel reinforced high strength concrete beams under deflection control loading conditions. Test variable includes volumetric percentage of steel fibers (0%, 1.5%, 3%, 4%, 5%). The plain concrete strength was 30MPa. The monotonic concentrated load was applied at the center of the beam, the relative deflection was measured, and demec points were used to determine curvature of the beam. Load-deflection and moment-curvature diagrams have been obtained and plotted for each beam individually. Test results indicate that higher fiber content considerably improves flexural behavior and provides... 

This article is intended to highlight the effectiveness of longitudinal Glass Fiber Reinforced Polymer (GFRP) bars in combination with GFRP sheets on the flexural capacity of Reinforced Concrete (RC) columns. Seven half-scale RC columns including five strengthened and two control unstrengthened specimens were experimentally tested under axial and cyclic lateral loads. The strengthened columns with two different longitudinal GFRP bar ratios were tested under three different axial load levels. The flexural strength and ductility parameters of the specimens were calculated by obtaining their deformations and measuring the loads from load cells. The experimental results indicate significant... 

Foamy Al alloy SiCp composites of different densities ranging from 0.4 to 0.7g/cm3 were manufactured by melt-foaming process, which consisted of direct CaCO3 addition into the molten A356 aluminum bath. Mechanical properties and morphological observations indicated that the three-stage deformation mechanism of typical cellular foams is dominant in the produced A356 aluminum foams. Middle-stage stress plateau shrinkage plus compressive strength and bending stress enhancements were observed in denser foams. With the same Al/SiCp ratio, energy absorption ability and plastic collapse strength of the closed-cell foams were increased with the foam density. Doubling cell-face bending effects... 

The application of superabsorbent polymer (SAP) as an internal curing agent for cement based composites results in benefits such as reduced autogenous shrinkage and cracking. However, a reduction in compressive and flexural strength usually occurs due to the empty voids remained in the matrix after deswelling of SAP particles. Nanoparticles are good candidates for improving the mechanical performance of cementitious materials, due to their multiple mechanisms of action, not the least their high pozzolanic activity.In the present work, the capability of amorphous nano-SiO2 (NS) as the most widely used nanoparticle in cementitious materials, for retrieving mechanical properties of... 

The environmental impact of asbestos fibers on human health and their consequent safety-related problems indicate that there is a significant need to replace this material in all asbestos-containing products. Many different types of fibers have been introduced to replace asbestos fibers. In this study, the performance of silica nano-particles combined with waste paper pulp fibers (sulfite fibers) has been investigated. Different mechanical (compressive and flexural strengths and bending performance), durability (water absorption), physical (bulk density and flowability), and microstructural (scanning electron microscopy) tests were conducted to examine the properties of manufactured green... 

Nanocrystalline hydroxyapatite (nHA) of 50 nm average diameter and length to diameter ratio of >3 was synthesized by biomimetic method. Non-isothermal sintering improved densification behavior and mechanical properties of apatite to 0.88 maximum fractional density, 70MPa bending strength, 148MPa compressive strength and 2.53GPa microhardness at sintering temperature of 1250°C. Higher sintering temperatures resulted in the decomposition of the apatite and in-situ biphasic calcium phosphate HAP/TCP formation. This process lowered apatite densification and weakened mechanical properties of the sintered specimen. Transmission electron microscopy (TEM), x-ray diffraction (XRD) and field emission... 

Semisolid stir joining has been under deliberation as a possible method for joining of copper alloys. In this study, the effect of temperature and rotational speed of stirrer on macrostructure evaluation and mechanical properties of samples were investigated. Optical microscopy and X-ray diffraction were performed for macro and microstructural analysis. A uniform micro-hardness profile was attained by semisolid stir joining method. The ultimate shear strength and bending strength of welded samples were improved in comparison with the cast sample. There is also lower area porosity in welded samples than the cast metal. The mechanical properties were improved by increasing temperature and... 

This paper presents the results of an experimental study on retrofitting RC beams using FRP strengthening and RC jacketing. Three-point loadings are applied to twelve strengthened beams and three reference specimens to put the two techniques into perspective. Formation of first cracks, FRP debonding, and onset of concrete crushing are compared and discussed. Load-deflection behavior, failure modes, and crack propagation patterns are studied extensively. The experiments demonstrate that the RC jacketed beams exhibit a flexural failure identical to the reference beams. However, the FRP strengthened beams fail in a relatively small deflection due to the premature FRP debonding. Furthermore, the... 

Hydroelastic effect in bottom slamming problem of high-speed craft is one of the most challenging issues in structural design. In this paper, numerical method is used to investigate the hydroelastic effect in bottom-water impact analysis of high-speed monohull craft. Slamming with two viewpoints of rigid and elastic structures (hydroelastic effect) is modelled by coupled computational fluid dynamic (CFD) and finite element method (FEM) techniques. The results showed that considering hydroelastic effect, especially in high-impact speed, reduces the structural deformations and stresses compared with quasi-statistic analysis. The effect of different parameters, such as boundary condition, plate... 

Up to 8wt. % of Nano-iron oxide was added to CaO refractory matrix. The crystalline phases and microstructure characteristics of specimens sintered at 1650°C for 5h in an electric furnace were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The physical properties are reported in terms of bulk density, apparent porosity and hydration resistance. The mechanical behavior was studied by a cold crushing strength (CCS) and flexural strength at 1200°C test. As a result, it was found that the presence of Nano-iron oxide in the CaO refractory matrix induced 2CaO.Fe2O3 (C2F), CaO.Fe2O3 (CF) and 3CaO.Al2O3 (C3A) phase's formation, which improved the sintering... 

The high hydration potential of CaO and MgO phases restricted the application of Mag-Dol refractory composites. In this study, the impact of nano-silica (SiO2) addition on the physical, mechanical, thermo-mechanical as well as microstructure of Mag-Dol refractory composites is investigated. Mag-Dol compositions were prepared by using calcined dolomite and magnesite particles (micron, 0–1, 1–3, 3–5, and 5–8 mm), liquid resin, and 0, 0.5, 1, 1.5, 2, and 2.5 wt% nano SiO2 as additives. Specimens were heated up to 1650 °C for the 3 h soaking period. Fired specimens were characterized by physical (apparent porosity, bulk density, and hydration resistance), mechanical (cold crushing strength), and... 

This research investigates the flexural behavior of a polymer concrete beam/pile encased with carbon fiber sleeve. The mechanical properties of carbon fiber sleeves in tension and cement and polymer concrete in compression were determined. Polymer concrete beams were tested in flexure to determine the bending moment capacity. Then, the test results were compared to the theoretical model results. Finally, a parametric study was conducted to determine the influence of beam/pile parameters on the capacity of the element. Based on the investigation, carbon fiber sleeve filled with polymer concrete exhibits outstanding structural performance including ductility and bending capacity. © 2017 Taylor... 

The present work developed a mixed-mode cohesive zone model (CZM) with a mode I failure criterion to predict the delamination bending loads of multilayer, composite printed circuit boards (PCBs) assembled with soldered ball grid array (BGA) components that were reinforced with an underfill epoxy adhesive. Two different delamination modes were observed in these microelectronic assemblies: delamination at the interface between the solder mask and the first conducting layer of the PCB, and PCB subsurface delamination at the interface between the epoxy and glass fibers of one of the prepreg layers. The cohesive parameters for each of the two crack paths were obtained from fracture tests of... 

The present work developed a mixed-mode cohesive zone model (CZM) with a mode I failure criterion to predict the delamination bending loads of multilayer, composite printed circuit boards (PCBs) assembled with soldered ball grid array (BGA) components that were reinforced with an underfill epoxy adhesive. Two different delamination modes were observed in these microelectronic assemblies: delamination at the interface between the solder mask and the first conducting layer of the PCB, and PCB subsurface delamination at the interface between the epoxy and glass fibers of one of the prepreg layers. The cohesive parameters for each of the two crack paths were obtained from fracture tests of... 

This paper investigated the combined utilization of recycled waste ceramic aggregate (RWCA) and waste carpet fibers (WCFs) in high strength concrete (HSC). Concrete mixes containing different percentages of RWCA including 20%, 40%, 60% (by weight) as partial replacement of natural coarse aggregate (NCA) were prepared. To enhance the tensile and flexural strength of concrete, 1.0% (by volume) WCF was added to the mixes. The slump and density of the fresh concrete were evaluated, both of which demonstrated a decreasing trend with incorporation of RWCA and WCF. With regard to the hardened concrete, replacing 40% of NCA with RWCA led to the optimum mechanical properties and increased the... 

The relation between process parameters and properties of polycarbonate (PC) sheet after friction stir welding (FSW) was investigated. Effects of FSW tool rotation speed (ω), travelling speed (V), tilt angle (α) and plunge depth on material flow, joint tensile strength, flexural strength, impact energy and hardness were investigated. It is shown that at low and high levels of heat input sound joints cannot be attained. At low heat inputs, the local temperature is not high enough to decrease the viscosity of the polymer to fill the interface, and thus voids and large planar cracks are formed in the joint root and stir zone. At high heat inputs, expelling of materials due to high peak... 

This research investigates the flexural behavior of a polymer concrete beam/pile encased with carbon fiber sleeve. The mechanical properties of carbon fiber sleeves in tension and cement and polymer concrete in compression were determined. Polymer concrete beams were tested in flexure to determine the bending moment capacity. Then, the test results were compared to the theoretical model results. Finally, a parametric study was conducted to determine the influence of beam/pile parameters on the capacity of the element. Based on the investigation, carbon fiber sleeve filled with polymer concrete exhibits outstanding structural performance including ductility and bending capacity