The low temperature perovskite-type calcium titanate (CaTiO3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route. The prepared sol had a narrow particle size distribution about 17 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that, the synthesized powders had highly pure and crystallized CaTiO3 structure with preferable orientation growth along (1 2 1) direction at 400-800 °C. The activation energy of crystal growth was calculated 5.73 kJ/mol. Furthermore, transmission electron microscope images showed that the average crystallite size of the powders annealed at 400 °C was around 3.5... 

Pechini process was used for preparation of three kinds of nanocrystalline powders of yttria-stabilized zirconia (YSZ): doped with 1.5 mol% nickel oxide, doped with 15 mol% ceria, and doped with 1.5 mol% nickel oxide plus 15 mol% ceria. Zirconium chloride, yttrium nitrate, cerium nitrate, nickel nitrate, citric acid and ethylene glycol were polymerized at 80 °C to produce a gel. XRD, SEM and TEM analyses were used to investigate the crystalline phases and microstructures of obtained compounds. The results of XRD revealed the formation of nanocrystalline powder at 900 °C. Morphology of the powder calcined at 900 °C, examined with a scanning electron microscope, showed that the presence of... 

Nanocrystalline TiO 2-Fe 2O 3 thin films and powders were prepared by a straightforward aqueous particulate sol-gel route at the low temperature of 300 °C. Titanium(IV) isopropoxide and iron(III) chloride were used as precursors, and hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powder crystallised at the low temperature of 300 °C, containing anatase-TiO 2 and hematite-Fe 2O 3 phases. Furthermore, it was found that Fe 2O 3 retarded the anatase-to-rutile transformation up to 500 °C. The activation energies for crystallite growth of TiO 2... 

A sonochemistry-based synthesis method was used to produce nanocrystalline nickel oxide powder with ∼20 nm average crystallite diameter from Ni(OH)2 precursor. Ultrasound waves were applied to the primary solution to intensify the Ni(OH)2 precipitation. Dried precipitates were calcined at 320 °C to form nanocrystalline NiO particles. The morphology of the produced powder was characterized by transmission electron microscopy. Using sonochemical waves resulted in lowering of the size of the nickel oxide crystallites. FT-IR spectroscopy and X-ray diffraction revealed high purity well-crystallized structure of the synthesized powder. Photoluminescence spectroscopy confirmed production of a wide... 

The low temperature perovskite-type strontium titanate (SrTiO 3) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route. The prepared sol had a narrow particle size distribution with hydrodynamic diameter of about 17 nm. X-ray diffraction (XRD) revealed that the synthesized powders had a perovskite-SrTiO 3 structure with preferable orientation growth along the (1 0 0) direction. TEM images showed that the average crystallite size of the powders annealed in the range 300-800°C was around 8 nm. FE-SEM analysis and AFM images revealed that the deposited thin films had mesoporous and nanocrystalline structure with the... 

Perovskite-type barium strontium titanate (BST) thin films and powders with nanocrystalline and mesoporous structure were prepared by a straightforward particulate sol-gel route at room temperature. The prepared sol had a narrow particle size distribution of about 20 nm. X-ray diffraction (XRD) revealed that phase composition and preferable orientation growth of BST depended upon the annealing temperature. Transmission electron microscope (TEM) images showed that the crystallite size of the powders decreased with increasing annealing temperature from 8 nm at 25 °C down to 5 nm at 800 °C. Field emission scanning electron microscope (FE-SEM) analysis and atomic force microscope (AFM) images... 

In micron-scale, powder consolidation process is driven by diffusion phenomenon, while in nano-scale the higher surface energy of particles leads to some anomalous behaviors within the process. In order to investigate the nano-sintering occurrence, an atomistic approach is employed via molecular dynamics simulations. Within this approach, the effect of particle size and temperature is examined. The study of particle structure emphasizes on a transition on the governing mechanism of process depending on the material energy levels. The results show that in a specific particle size at low temperatures, the main sintering mechanism is the plastic deformation, while at elevated temperatures it... 

Properties of FeCo nanocrystalline intermetallic powders prepared by salt-matrix hydrogen reduction of a milled Fe 2O 3-Co 3O 4 mixture were investigated. The product of 72 ks ball-milling at 350 rpm was CoFe 2O 4 nanopowder. Reduction of this powder for 3.6 ks by hydrogen at 750 °C resulted in the formation of Fe 0.67Co 0.33 stoichiometric compound. Scanning electron microscopy, electron dispersive spectrometry, X-ray diffraction and vibrating sample magnetometry were used to characterize the nanopowder. Using a salt-matrix (NaCl as a dispersion medium) resulted in the decrease of the reduction temperature and improvement of the morphology and magnetic properties of the nanopowder.... 

Nanocrystalline nickel titanate (NiTiO3) thin films and powders with mesoporous structure were produced at the low temperature of 500 °C by a straightforward particulate sol-gel route. The sols were prepared in various Ni:Ti molar ratios. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained mixtures of the NiTiO 3 and NiO phases, as well as the anatase-TiO2 and the rutile-TiO2 depending on the annealing temperature and Ni:Ti molar ratio. Moreover, it was found that Ni:Ti molar ratio influences the preferable orientation growth of the nickel titanate, being on (202) planes for the nickel dominant powders (Ni:Ti ≥ 75:25) and on (104) planes for the... 

Nanocrystalline neodymium titanium oxide thin films and powders with different phase compositions with mesoporous structure were produced by a straightforward particulate sol-gel route. The sols were prepared in various Nd:Ti molar ratios and they showed a narrow particle size distribution in the range 20-26 nm. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders contained mixtures of Nd4Ti9O24, Nd2Ti4O11, Nd3Ti4O12 for titanium dominant powders (Nd:Ti ≤ 45:60), mixtures of Nd2TiO5 and Nd2O3 for neodymium dominant powders (Nd:Ti ≥ 75:25) and pure Nd3Ti4O12 phase for equal molar ratio of Nd:Ti, depending on the annealing temperature and Nd:Ti... 

In this work, nanocrystalline Al6063 composite powder reinforced with nanometric oxide ceramic particles was synthesized via an in situ solid-gas reaction during high-energy mechanical alloying under a mixture of argon-oxygen atmosphere. The effect of oxygen volume fraction on the morphological evolution and microstructural changes during mechanical alloying was studied by various analytical techniques including optical and electron microscopy, X-ray diffraction, laser particle size analysis, apparent density measurement, and microhardness test. The reactive mechanical alloying resulted in the formation of amorphous Al- and Al-Mg-Si-Fe oxides with a size range of 40-100. nm and volume... 

Low temperature lithium titanate compounds (i.e., Li4Ti 5O12 and Li2TiO3) with nanocrystalline and mesoporous structure were prepared by a straightforward aqueous particulate sol-gel route. The effect of Li:Ti molar ratio was studied on crystallisation behaviour of lithium titanates. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders were crystallised at the low temperature of 500 °C and the short annealing time of 1 h. Moreover, it was found that Li:Ti molar ratio and annealing temperature influence the preferable orientation growth of the lithium titanate compounds. Transmission electron microscope (TEM) images showed that the average... 

Nanocrystalline zinc titanate (ZnTiO3) thin films and powders with purity of 94% were produced at the low sintering temperature of 500 °C and the short sintering time of 1 h by a straightforward aqueous particulate sol-gel route. The effect of Zn:Ti molar ratio was studied on the crystallisation behaviour of zinc titanates. The prepared sols showed a narrow particle size distribution in the range 17-19 nm. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powders contained mixtures of the rhombohedral-ZnTiO3, cubic-ZnO, cubic-Zn2TiO4 phases, as well as the anatase-TiO2 and the rutile-TiO2 depending on the sintering temperature and Zn:Ti molar ratio.... 

In this study, SnO 2-based varistors were prepared from mechanically activated nanocrystalline powders. Nanocrystalline powders were derived by subjecting the initial powders to intensive high-energy activation with different times and ball to powder ratio. The effect of activation parameters on the powder properties and sintering temperature, as well as microstructural, micro-electrical and macro-electrical properties of the final specimens was evaluated. Varistors derived from high-energy mechanical activation exhibit a higher density (98.3% relative density) and more refined microstructure upon sintering at 1,300 °C in comparison varistors prepared from conventional powders. Breakdown... 

Nanocrystalline Al-5vol%Al2O3 nanocomposite was synthesised by mechanical milling of a mixture containing nanometric alumina with an average particle size of 35 nm. Morphology of as-synthesised powder was investigated by SEM while crystallite size of Al matrix was determined by XRD analysis. The results confirmed formation of nanocrystalline Al matrix induced by severe plastic deformation during mechanical milling. Nanocomposite bars were produced by hot powder extrusion route. TEM investigation of as-extruded nanocomposite revealed formation of elongated grains along the extrusion direction decorated by alumina nanoparticles. Tensile and compressive properties of as-extruded nanocomposite... 

Mn1.5Co1.5O4 oxide spinels are widely used as protective coatings for stainless steel interconnects within planar solid oxide fuel cell stacks. Containing both cubic and tetragonal crystalline phases, these Mn/Co oxide spinels exhibit favorable thermal stability and electronic conductivity for the SOFC interconnect application. Slurry-based coating applications of Mn/Co oxides require precursor powders, which can benefit from being nano-structured. In this study, the sol-gel synthesis of nanocrystalline Mn1.5Co1.5O4 spinel is investigated. The decomposition of sol-gel precursors, as well as the crystalline phase structures and microstructures of the product Mn1.5Co1.5O4 are characterized by... 

In this paper fabrication of a 0-3 ceramic/ceramic composite lead zirconate titanate, Pb(Zr0.52Ti0.48)O3 thin film has been presented and then a pressure sensor based on multilayer thin-film PZT diaphragm contain of Lead Zirconate Titanate nanocrystalline powders was designed, modeled and optimized. This multilayer diaphragm in general acts as sensor or actuator. ANSYS was used for simulation of diaphragm. Dynamics characteristics of this multilayer diaphragm have been investigated. By this simulation the effective parameters of the multilayer PZT diaphragm for improving the performance of a pressure sensor in different ranges of pressure are optimized. The optimized thickness ratio of PZT... 

Recently, co-powder injection molding process (2C-PIM) has attained considerable interest to fabricate complex-shaped functional materials. The aim of this work is to study the sintering compatibility between nanocrystalline yttria-stabilized zirconia (3Y-TZP) and PIM grade 430L stainless steel (SS) powders, which is the utmost important step in the 2C-PIM process. To evaluate the mismatch strain development during the co-sintering, the isothermal and nonisothermal behaviors of the ceramic and metal powders were studied. Small bilayers of 3Y-TZP/430L were made by a powder metallurgy technique and the feasibility of simultaneous sintering and joining of the composite layer was examined.... 

Low-temperature perovskite-type cadmium titanate (CdTiO3) with a nanocrystalline and mesoporous structure was prepared at various Ti:Cd molar ratios by a straightforward particulate sol-gel route. The prepared sols had a narrow particle size distribution, in the range 23-26 nm. X-ray diffraction and Fourier transform infrared spectroscopy revealed that the powders contained a mixture of ilmenite-CdTiO3, perovskite-CdTiO3, anatase and rutile phases, depending on the annealing temperature and the Ti:Cd molar ratio. Perovskite-CdTiO3 was the major type obtained from cadmium-prominent powders at low temperature, whereas ilmenite-CdTiO3 was the major type obtained from titanium-prominent powders... 

Highly stable, water-based barium titanate (BaTiO3) sols were developed by a low cost and straightforward sol-gel process. Nanocrystalline barium titanate thin films and powders with various Ba:Ti atomic ratios were produced from the aqueous sols. The prepared sols had a narrow particle size distribution in the range 21-23 nm and they were stable over 5 months. X-ray diffraction pattern revealed that powders contained mixture of hexagonal- or perovskite-BaTiO3 as well as a trace of Ba2Ti 13O22 and Ba4Ti2O27 phases, depending on annealing temperature and Ba:Ti atomic ratio. Highly pure barium titanate with cubic perovskite structure achieved with Ba:Ti = 50:50 atomic ratio at the high...