γ-Alumina is used to catalyze the Cannizzaro reaction in the absence of any base under microwave irradiation in high yields. In the case of terephthalaldehyde the reaction is carried out with high selectivity  

Chitosan was modified with polyacrylonitrile (PAN) through ceric-initiated graft copolymerization. The chitosan-g-PAN product was saponified using sodium hydroxide aqueous solution to prepare a novel superabsorbent hydrogel, H-chitoPAN. Duration of completing the saponification reaction as well as the water absorbency capacity of the hydrogel was decreased with increasing the alkaline concentration. Either chitosan-g-PAN or H-chitoPAN was characterized by FTIR spectroscopy and DSC, TGA, and DTG thermal methods. According to FTIR, all the nitrile groups were converted to carboxylate and carboxamide groups. Both modified chitosans exhibited enhanced thermal stability over chitosan. The... 

Carboxymethylcellulose sodium salt (CMC) was doubly modified to prepare a novel poly(acrylamidoxime) chelating resin. Acrylonitrile was firstly graft polymerized onto CMC using cerium ammonium nitrate as an initiator. The polyacrylonitrile (PAN) grafted CMC was then amidoximized via treatment with hydroxylamine to prepare the ion exchange resin. The sorption capacity of the resin towards bivalent metal ions was evaluated while varying the pH, the loading of the PAN and the initial metal ion concentration. The adsorption kinetics were investigated for the cupric ion. The chelating resin exhibited very high metal sorption capacity in comparison with either synthetic or polysaccharide-based... 

As the first part of a continued research on conversion of carboxymethyl cellulosesodium salt (CMC) to useful biopolymer-based materials, large numbers of cyanide functional groups were introduced onto CMC by grafting with polyacrylonitrile (PAN). The graft copolymerization reactions were carried out under nitrogen atmosphere using ceric ammonium nitrate (CAN) as an initiator. Evidence of grafting was obtained by comparing FTIR spectra of CMC and the graft copolymer as well as solubility characteristics of the products. The synthetic conditions were systematically optimized through studying the effective factors including temperature and concentrations of initiator, acrylonitrile monomer,... 

A novel kappa-carrageenan (C)-based superabsorbing hydrogel was synthesized through graft copolymerization of acrylamide (AAm) onto a C substrate in the presence of a crosslinking agent. The crosslinked C-poly(AAm) polymer graft was partially hydrolyzed in alkaline medium to yield a superabsorbent resin, H-carragPAM. The resin structure was confirmed using FTIR spectroscopy. The variables of graft copolymerization (monomer, initiator, polysaccharide and crosslinker concentration, reaction temperature and time as well as stirrer speed) that affected on the ultimate water-swelling capacity were optimized. The time-temperature variation of the copolymerization was investigated in terms of the... 

In this paper, design, simulation and optimization of a novel electrothermally-activated polymeric microactuator capable of generating combination of bidirectional lateral and rotational motions are presented. The composite structure of this actuator is consisted of a symmetric meandered shape silicon skeleton, a SU8 thermal expandable polymer and a thin film chrome layer heater. This actuator is controlled by applying appropriate voltages on its four terminals. With the purpose of dimension optimization, a numerical parametric study is executed. The modeled actuator which is 1560 ?m long, 156 ?m wide and 30 ?m thick, demonstrates a remarkable lateral displacement of 23 ?m at power... 

This paper describes how to find optimal operating conditions of three controlling parameters, i.e. temperature, transmembrane pressure (TMP), and cross-flow velocity (CFV) for maximizing the permeate flux and total organic carbons (TOC) rejection, and minimizing the fouling resistance using Taguchi method in ultrafiltration (UF) treatment of the real produced water. At first, the optimal operating conditions were found at a temperature of 45°C, TMP = 4 bar, and CFV of 2.25 m/s. To determine the most significant parameters affecting the response parameters, an analysis of variance was employed. In the second stage, performance of applied polymeric membrane in the UF system was studied under... 

In this study, polypropylene/carbon nanotube nanocomposites were prepared via in situ polymerization using a bi-supported Ziegler-Natta catalytic system. In this system, magnesium ethoxide and multiwall carbon nanotubes (MWCNTs) are jointly used as catalyst supports. SEM images reveal the distribution and quite good dispersion of MWCNTs throughout the polypropylene (PP) matrix. The thermal properties of the samples were examined using DSC and TGA tests. The results show that the crystallization temperature of the nanocomposites significantly increases while the melting point is not markedly affected. In addition, the thermal stability is improved. The melt rheological properties of PP/MWCNT... 

This work, which is a part of our ongoing studies on developing conductive scaffolds for nerve tissue engineering, reports synthesis of highly conductive binary-doped polyaniline nanoparticles and polyaniline/graphene nanocomposites. The samples were synthesized through chemical oxidation of aniline via in situ emulsion polymerization method in presence of hydrochloric acid and sodium dodecyl sulfate. Graphene nanosheets were also prepared via modified Hummer's method followed by chemical reduction using hydrazine monohydrate. Electrical conductivity measurements using a standard four-point probe technique with FTIR and UV-vis studies revealed that conductive binary-doped emeraldine salt... 

Optimization of operational conditions for the preparation of Ultrahigh-molecular-weight polyethylene (UHMWPE)/Graphene nanocomposites with Ziegler-Natta catalyst was carried out via response surface methodology (RSM). This study deals with the optimization of process variables to optimize the productivity and molecular weight. A three-factor, three-level Box-Behnken design with temperature (X1), monomer pressure (X2), and [Al]/[Ti] molar ratio (X3) as the independent variables were selected for the study. The dependent variables were productivity and molecular weights of the final nanocomposites. It was developed by using the three parameters at three levels including 50, 60, and 70°C for... 

We present the preparation of polypropylene (PP)/fumed silica (FS) nanocomposites via in situ polymerization in this article. The approach includes preparation and utilization of a bisupported Ziegler-Natta catalytic system in which magnesium ethoxide and FS are used as conjugate supports of the catalyst. Catalyst preparation and polymerization processes are carried out in the slurry phase and under argon atmosphere. Scanning electron microscopy images show a good dispersion of the FS throughout the PP matrix. Results from differential scanning calorimetry reveal that the crystallization temperature of prepared nanocomposites increases by increasing FS loading. Also, crystal content of... 

The present paper demonstrates the capability of narrow graphene nanoribbons (GNRs) in constructing new sensing platforms. Graphene nanoribbons have been synthesized via a simple solvothermal route through unzipping of carbon nanotubes, which was confirmed by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and Raman spectroscopy analysis. These narrow carbon sheets were used to form a composite film by in-situ electro-polymerization with aniline. The produced graphene nanoribbon/polyaniline (GNR/PANI) composite film showed impressive performance in electrochemical determination of dobutamine (DBT). Under optimal conditions, in comparison to... 

A rapid, convenient and reliable method for microextraction in packed syringe (MEPS) of the loop diuretic furosemide (FUR) in urine along with high-performance liquid chromatography (HPLC) was developed. A nanocomposite based on silver nanoparticles/polyaniline (Ag-NPs/PANI) was synthesized and used as the MEPS packing material. This nanocomposite was prepared conveniently using interfacial polymerization without the need for any templates or functional dopants. The feasibility of the synthesized nanocomposites was examined by isolation of FUR from diluted urine samples. After extraction, the analyte was desorbed by 200 μL of methanol. It was then dried and the residue was dissolved in 30 μL... 

Poly(amidoamine) dendrimer (PAMAM) was successfully functionalized by chlorosulfonic acid to form an strong ionic acid catalyst. The resulting polymeric catalyst was shown to be an efficient catalyst for the synthesis of 1,1-diacetyl from aldehydes under free solvent conditions at room temperature. Also, the deprotection of the resulting aldehydes was investigated under catalytic conditions. The Hammett acidity function of catalyst showed that catalyst is a strong Brønsted acid. Due to the multi-functional nature of PAMAM, the catalyst has high loading level of acidic protons  

Ultrahigh-molecular-weight polyethylene (UHMWPE)/graphene nanocomposites with molecular weights as high as 3 × 106 g/mol were prepared via in situ polymerization using a bi-supported Ziegler-Natta catalytic system. Effects of [Al]/[Ti] molar ratio, temperature, monomer pressure, and polymerization time on productivity of the catalyst have been investigated. Increasing [Al]/[Ti] molar ratio from 128 to 320, increased productivity from 1667 g PE/mmol Ti.h to maximum value which was 2420 g PE/mmol Ti.h. Further [Al]/[Ti] ratio decreased the productivity. Reaction temperature effect investigation reveals that the optimal activity was obtained at 60°C. the polymerization productivity increases... 

A multicomponent polysaccharide obtained from dried tubers of certain natural terrestrial orchids was chemically modified by sulfonation using chlorosulfonic acid-dimethylformamide (HClSO3-DMF) complex as a reagent. For a structural characterization of salep sulfate 1H nuclear magnetic resonance (NMR), Fourier transform infrared (FTIR) spectra, and Thermogravimetric analysis (TGA) curves were recorded. The sulfate content of modified salep was determined using elemental analysis. This modified biopolymer was used to prepare a new environment-friendly heavy metal ion adsorbent, salep sulfate-graft-polyacrylic acid hydrogel (SS-g-PAA). Swelling rate and equilibrium water absorbency in various... 

A series of 3-cyano-2-pyridone derivatives were synthesized by one-pot four-component condensation reaction involving a benzaldehyde derivative, alkyl cyanoacetate, acyclic or cyclic ketones, and ammonium acetate in reflux condition. The X-ray structure of the products 5a and 5d confirm symmetric dimers via hydrogen bonding interactions between individual pyridine molecules showing, in addition, also π-π stacking interactions  

A novel basic poly(ionic liquid) (PIL) was synthesized by miniemulsion polymerization of ionic liquid monomer 1-ethyl-3-vinylimidazolium bromide [EVim][Br] which was cross-linked by ionic liquid cross-linker 1,4-butanediyl-3,3'-bis-l-vinylimidazolium dibromide (BVD). Exchange of bromide anions in PIL nanogel with hydroxide, produced a supported basic ionic liquid catalyst. The catalytic performances of PIL nanogel with a size of about 200. nm was evaluated in the synthesis of 4. H-benzo[. b]pyrans by multi-component reaction in water. The present protocol represents a simple, ecologically safe and cost-effective route to synthesize 4. H-benzo[. b]pyrans with high products yield  

A new analytical formulation is presented to study the steady-state creep in short fiber composites using complex variable method. In this new approach, both the fiber and matrix creep at low stresses and temperatures. To analyze the crept fiber, a plane stress model was used. Important novelties of the present analytical method are determination of displacement rates with proper boundary conditions in the crept fibers and also using the complex variable method in creep analyzing. It is noteworthy that the method can be useful to study the creep behavior in polymeric matrix composites due to their high capability of creep. Moreover, another significant application of the present method is to... 

Potential applications of the molecularly imprinted polymers (MIPs) demand physical configurations in different size ranges. Nowadays, research on MIPs is focused on the development of new or improved morphologies, which involves control and modification of the different parameters during the synthesis. In this study, the effect of different synthesis conditions on the particle size and morphology is investigated. Carbamazepine-imprinted polymers were prepared using precipitation polymerization under various conditions such as: the amounts of cross-linker and functional monomers, initiator, porogen, temperature and time of polymerization. We studied the polymerization conditions to obtain...