Sharif Digital Repository

Ta0.8Hf0.2C ceramic has the highest melting point among the known materials (4000 °C). However, this high melting point makes the ceramic difficult to be sintered at temperatures lower than 2300 °C, pressurelessly. The purpose of this study is to consolidate Ta 0.8Hf0.2C UHTC by pressureless sintering at 2000 °C using MoSi2 as sintering aid. In this regard, effect of different amounts of MoSi2 on sintering behavior of Ta0.8Hf 0.2 UHTC was investigated. It was observed that condensation of the UHTC after sintering at 2000 °C was enhanced by increasing MoSi2 content and the highest relative density of 95% was obtained in the presence of 24 vol.% MoSi2. XRD pattern of the sintered UHTC... 

ZnFe2O4 nanoparticles have been successfully prepared through a controlled microwave-assisted co-precipitation. X-ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR), Scanning Electron Microscopy (SEM) and Vibrating Sample Magnetometer (VSM) were used for the structural, morphological and magnetic investigation of the product. SEM micrographs of ZnFe2O4 nanopowder also reveal that nanoparticles have spherical shape. Average particle size was obtained as 12 nm from XRD. Catalytic activity of ZnFe2O4 nanopowder for O-acylation of alcohol and phenol has been investigated. A trace amount of ZnFe2O4 has been effectively used as a nanocatalyst for the acylation of alcohol and... 

Cobalt is the most common binder in cemented carbides industry. However, there are some interests in use of alternatives. The similarity in properties has made nickel the first choice. In the present work, the effect of initial composition on modern hardmetals containing transition metal carbides/carbonitrides that are called "cemented carbonitrides" with nickel as binder was investigated. Change in quantity of additive carbides and tungsten to carbon (C/W) weight ratio through applying metallic tungsten powder in primary powder mixture had some effects on final hardness, transverse rupture strength, and microstructure of studied alloys. Addition of vanadium carbide not more than 0.2 wt.%,... 

In this research, it is shown that the production of bimetallic Al/Cu rod by cold ECAE process is feasible. The mechanism of the cold weld between the copper sheath and aluminum core is assessed using the characteristics of the mating surfaces both theoretically and by examining the SEM micrographs of the peeled surfaces. It is shown that the stretch produced by the shear strain in the process leads to the fracture of the work-hardened layer of the mating surfaces and then by extruding the virgin metal through the cavities of the cracks a cold weld is developed between the sheath and core of the rod. To achieve the cold weld, a threshold surface stretch of about 59% is required. It is shown... 

Utilizing the so-called tube spinning, a cold-bonding process entitled as "spin-bonding" is developed to produce seamless thin-walled clad tubes and cylinders. By this method, two layers of AA 1050 tubes were successfully bonded together to form a clad tube at room temperature. Based on mechanical aspects of the tube spinning process, the mechanism of spin-bonding is explained in two stages: surface preparation before occurrence of a stable bond and bond strengthening thereafter. The effects of process temperature, thickness reduction, feed rate and roller attack angle as the parameters of tube spinning on the bond strength are studied. It is shown that the bond strength increases by... 

In this paper fabrication of a 0-3 ceramic/ceramic composite lead zirconate titanate, Pb(Zr0.52Ti0.48)O3 thin film has been presented and then a pressure sensor based on multilayer thin-film PZT diaphragm contain of Lead Zirconate Titanate nanocrystalline powders was designed, modeled and optimized. This multilayer diaphragm in general acts as sensor or actuator. ANSYS was used for simulation of diaphragm. Dynamics characteristics of this multilayer diaphragm have been investigated. By this simulation the effective parameters of the multilayer PZT diaphragm for improving the performance of a pressure sensor in different ranges of pressure are optimized. The optimized thickness ratio of PZT... 

Recent uses of intelligent composites in biomedical appliances aggrandize the necessity of bonding-strength improvement in NiTi/silicone matrix interface. SEM micrographs and pull-out tests are employed to determine the strength of the NiTi/silicone bonds in a flexible composite piece. Greater adhesion strengths are obtained due to the presence of thin oxide layer, surface roughness and frictional forces between the embedded-wires and the contacting phase. Effect of curing treatment on phase transformation temperatures of the wires is determined by electrical resistivity (ER) measurements. Results show that the curing treatment shifts the transition points of the wires towards higher... 

Lead silicate glasses (LSGs) have high gamma-ray attenuation but low chemical durability properties. In this work, LSGs with (55.5-68.5 wt%) PbO content containing ZrO2 and TiO2 additions were produced. The chemical corrosion of various produced LSGs in 0.5 N HNO3 aqueous solution and determination of their gamma-ray attenuation coefficients for 60Co and 137Cs sources were investigated. The weight loss measurements, the SEM micrographs, the EDS analysis of the sample surfaces and the ICP analysis of solution were used to characterize the dissolution process. The effects of PbO content, ZrO2 and TiO2 additives on chemical corrosion, and also the effect of PbO on gamma-ray attenuation... 

In spite of various works which were carried out on CdO and porous Si (PSi) separately, the interesting properties of CdO/PSi/Si system are not known well. In this work, we study the photoconductivity of deposited CdO layer on PSi/Si system. PS and CdO layers were prepared by electrochemical anodisation of p-type crystalline silicon and pulsed laser deposition (PLD) of cadmium oxide target. Then samples were annealed in air at 500°C to increase their optical transmissions to a value as large as 90% for wavelengths above 700 nm. The XRD study reveals that the annealed films are polycrystalline with grain size of about 25 nm. SEM micrograph of the CdO/PSi/Si system indicates that CdO layer has... 

Two-stage chemical deposition (TSCD) technique is used to produce ZnO, Mn2O3 and NiO films on soda-lime glass (SL-G) from an aqueous solution of zinc, manganese and nickel complex, respectively. The TSCD method enables the deposition of metal oxide thin films with a thickness which can be controlled during the preparation procedure. The ZnO, Mn 2O3 and NiO thin films were polycrystalline films which were adherent well to the substrates. The SEM micrographs clearly indicate that the zinc oxide layer is composed of oval shaped crystallites preferably orientated perpendicular to the surface of the substrate. The Mn 2O3 and NiO layers were closely packed on the substrate. These particles seem to...