Sharif Digital Repository

In this research, the hot and warm rolling of stainless steel 304 was studied. First the rolling process was simulated using Finite Element Method software ABAQUS and the distribution of temperature and strain in the process under discontinuous conditions were predicted. Next, hot and warm rolling of stainless steel 304 under different conditions was carried out. Specimens were cut and subject to mechanical testing, metallography and electron microscopic studies. Data obtained from these experiments and the predicted trends from ABAQUS were compared, therefore studying the effect of different parameters on the microstructure and mechanical properties of the rolled specimen. Results indicate... 

A mathematical model was developed to assess thermomechanical behavior of work rolls during warm rolling processes of AA2017. A combined finite element analysis-slab method was first developed to determine thermal and mechanical responses of the strip being rolled under steady-state conditions; Then, the calculated roll pressure and temperature field were utilized as the governing boundary conditions for the thermomechanical problem of the work roll. Finally, the thermomechanical stresses within the work rolls were predicted by a thermoelastic finite element approach. The results indicate that, in warm strip rolling, thermal and mechanical stresses developed in the work rolls are comparable.... 

Lots of researches have been carried out on the severe plastic deformation (SPD) and annealing of the aluminum up to now. Due to the different annealing behavior of the severely deformed metals and on the other hand the necessity to the rollig for producing the thin SPD sheets, so the purpose of the recent study is producing the thinned sheets with applying the temperature simultaneously. Dislocations density increases by SPD so it confines their movement and cause to the higher strength of the material. Rolling of the SPDed sheets increase the mechanical properties. Grain boundary energy increases with this mechanical improvement and results in lower ductility. So, it is necessary to... 

Since the increase in the strength of metals resulting from the severe plastic deformation (SPD) leads to a reduction in their ductility, recently, several studies have been carried out on the deformation of metals. One if the goals has been increasing the ductility while maintaining the strength. In this project, copper is undergone severe plastic deformation in a constrained groove pressing (CGP) process. According to previous studies, it has been determined that with an optimal annealing process, not only the strength is not decreased, but also it is slightly increased and also the ductility is enhanced. Thus, in order to improve the surface of copper after CGP and also optimize its... 

In this study, thermo-mechanical behavior of an austenitic stainless steel AISI316L was investigated using mathematical modeling and experimental analysis during warm rolling process. First, the thermo-mechanical analysis was carried out employing the finite element software, Abaqus CAE, to assess temperature, strain, velocity and stress distribution during rolling. Then, rolling operations on 316L austenitic steel were performed under different working conditions while mechanical testing as well as microstructural observations were made on the rolled steels. Using simulation results and practical data, microstructural events and mechanical properties after warm rolling of stainless steel... 

In recent years, various research has been done on the severe deformation of low carbon steel sheets. One of the methods used is the pressing in the grooved die, only two passes of the pressing process in the grooved mold have been successful when applied to these sheets, but on the other hand, these two passes also lessen the sheet's ductility while increasing its strength. Due to the fact that the sheet surface produced by the pressing in the grooved die is not entirely smooth, the attempt in this project was to improve the ductility to some extent using warm rolling in addition to the smoothness of the surface using higher temperature while improving the strength or maintain it. To... 

In this research it has been attempted to suggest a modified retrogression and re- aging heat treatment on the sheet of AA7075 alloy with a thickness of 2 mm. The main aim of the research is to reduce the required duration of RRA process while maintaining the value of the conventional tensile strength achieving by the RRA process. This was performed by adding an intermediate warm rolling deformation during the RRA process. The rolling temperature was 180 °C and the rolling reductions were 30%, 40%, 50%. Moreover, the temperature of 170°C was selected as the re-aging temperature, for which the aging time of 0.5, 1, 1.5, 2, and 2.5 hours were examined. This temperature and times were chosen to...