Sharif Digital Repository

Ordered perpendicular TiO2 nanotubes (TNT) with 405 to 952 nm length and 60 to 90 nm diameter were grown via 40 to 120 min anodization of Ti6Al4V flat substrates. The samples were called TNT-40, -60, -80, -100, and -120. Vancomycin was loaded on the bare and anodized electrodes by separate immersion and electrophoretic (EP) deposition procedures. EP loading resulted in storage capacity of 5221.86 μg cm-2 for TNT-80 which was much higher than 1036.75 μg cm-2 of immersed sample. Drug release comprised of three stages: (i) burst release (78% for the bare, and 23% for the TNT-80 sample), (ii) gradual transport (21% for the bare, and 64% for the TNT-80 sample), and (iii) equilibrium. Transfer... 

We conduct an experimental investigation on the pool boiling enhancement in DI water on nanoporous surfaces. The surfaces are modified by anodic oxidation, and cavities with 2 mm diameter and pitches between 2.5 and 5 mm applied on them using EDM method filled with a two-part epoxy with low thermal conductivity properties. The capillary wicking action of the superhydrophilic nanoporous oxide layer enhances the rewetting and spreading of the liquid to dry-spots during boiling. The epoxy disks remain wet and prevent merging bubbles during the pool boiling experiment and a 2-D microflow is induced toward dried regions with synergic effects of nanoporous surface absorption, create a considerable... 

Room temperature gas sensing behavior of arrayed one-dimensional (1D) nickel nanowires (Ni NWs) are investigated using impedance spectroscopy. Ni nanowires synthesized via electrochemical deposition method based on anodic aluminum oxide (AAO) templates. Their structural characterization verified by scanning electron microscopy (SEM), x-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR) analysis. Impedance spectroscopy as an essential technique utilized to understand the mechanism of gas interaction with the wires through the changes in their electronic behavior. Bode and Nyquist plots with the real and imaginary impedances are plotted versus frequency range of 500 Hz... 

In this paper we report an efficient synthesis of hydrolyzed collagen-g-poly(sodium acrylate-co-2-hydroxyethyl aery late) hydrogel through chemical cross-linking by graft copolymerization of these two monomers onto the protein backbone in the presence of a cross-linker. Infrared spectroscopy and thermogravimetric analysis (TGA) were carried out to confirm the chemical structure of the hydrogel. Moreover, morphology of the samples was examined by scanning electron microscopy (SEM). To investigate the effect of monomer ratio on swelling behavior in various media three hydrogels with different acrylic acid/2-hydroxyethyl acrylate (AA/HEA) weight ratios were synthesized and swelling capacity was... 

A mixture of multi-walled carbon nanotube/graphite paste electrode modified with a salophen complex of cobalt was prepared and was applied for the study of the electrochemical behavior of 6-mercaptopurine (MP) using cyclic and differential pulse voltammetry (DPV). An excellent electrocatalytic activity toward the oxidation of MP was achieved, which led to a considerable lowering in the anodic overpotential and remarkable increase in the response sensitivity in comparison with unmodified electrode. Utilizing DPV method, a linear dynamic range of 1-100 μM with detection limit of 0.1 μM was obtained in phosphate buffer of pH 3.0. The electrochemical detection system was very stable, and the... 

An Al2O3/Si3N4 nanocomposite coating was successfully fabricated on commercial aluminum alloy. Hardness measurements, polarization and electrochemical impedance spectroscopy (EIS) were employed to study the mechanical and corrosion behaviors of the coatings. Field-Emission Scanning Electron Microscopy (FE-SEM) equipped with Energy Dispersive Spectroscopy (EDS) and X-ray diffraction (XRD) were utilized to characterize the surface morphology and phase composition of the coatings. Also, coatings abrasive wear properties were evaluated with a modified ASTM G105 standard. FE-SEM image, EDS and XRD analysis revealed the presence of Si3N4 in the coating. Furthermore, the results showed hardness of... 

Synthesis of novel natural-based superabsorbents with improved properties is of prime importance in many applications. In this article we report an efficient synthesis of new polysaccharide-based superabsorbent hybrid composing carrageenan, acrylic acid, sodium acrylate, and 2-hydroxyethyl acrylate through homogenous solution polymerization process. Infrared spectroscopy and thermogravimetric analysis (TGA) were carried out to confirm the chemical structure of the hydrogel. Moreover, morphology of the samples was examined by scanning electron microscopy (SEM). To deeper studies on the structure-property relation in SAP hydrogels, three hydrogels with different acrylic acid/2-hydroxyethyl... 

A carbon paste electrode (CPE) modified with 2,2′-[1,2 butanediylbis(nitriloethylidyne)]-bis-hydroquinone (BBNBH) and TiO2 nanoparticles was used for the sensitive voltammetric determination of epinephrine (EP). The electrochemical response characteristics of the modified electrode toward EP and acetaminophen (AC) were investigated by cyclic and differential pulse voltammetry (CV and DPV). The results showed an efficient catalytic activity of the electrode for the electrooxidation of EP, which leads to a reduction in its overpotential by more than 270 mV. The effects of pH and potential sweep rate on the mechanism of the electrode process were investigated. The modified electrode exhibits an... 

The preparation and electrochemical performance of the carbon nanotube-paste electrode modified with salophen complexes of cobalt(III) perchlorate, with various substituents on the salophen ligand, as well as their electrocatalytic activity toward the oxidation of N-acetylcysteine (NAC) is investigated. Several Schiff base complexes containing various nucleophilic and electrophilic functional groups were prepared, and their electrochemical characteristics for the electro-oxidation of NAC were evaluated using cyclic and differential pulse voltammetry (CV and DPV). The results revealed, the modified electrodes show an efficient and selective electrocatalytic activity toward the anodic... 

The most common reasons for hard-tissue implant failure are structural loosening and prosthetic infections. Hence, in this study, to overcome the first problem, different bioinspired coatings, including dual acid-etched, anodic TiO2 nanotubes array, anodic hierarchical titanium oxide (HO), micro- and nanostructured hydroxyapatite (HA) layers, and HA/chitosan (HA/CS) nanocomposite, were applied to the titanium alloy surfaces. X-ray diffraction and FTIR analysis demonstrated that the in situ HA/CS nanocomposite formed successfully. The MTT assay showed that all samples had excellent cell viability, with cell proliferation rates ranging from 120% to 150% after 10 days. The HO coating...