Sharif Digital Repository

Nanocrystalline TiO 2-Fe 2O 3 thin films and powders were prepared by a straightforward aqueous particulate sol-gel route at the low temperature of 300 °C. Titanium(IV) isopropoxide and iron(III) chloride were used as precursors, and hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the powder crystallised at the low temperature of 300 °C, containing anatase-TiO 2 and hematite-Fe 2O 3 phases. Furthermore, it was found that Fe 2O 3 retarded the anatase-to-rutile transformation up to 500 °C. The activation energies for crystallite growth of TiO 2... 

In this study, TiO 2-SiO 2 nanocomposite films with different amounts of SiO 2 were prepared by sol-gel process and were coated onto stainless steel 316L. The effect of addition of various amount of SiO 2 in the precursor solution on the photocatalysis, photo-generated hydrophilicity and self-cleaning property of TiO 2 thin films was investigated by X-ray diffraction, Fourier transform infrared spectroscopy, water contact angle measurements and UV spectroscopy. In the tested ranges of SiO 2 content and sintering temperature, the highest photocatalytic activity and self-cleaning property were observed in the 15 mol% SiO 2 sample sintered at 750 °C. Addition of less than 30 mol% SiO 2 had a... 

In this research, ultrahigh-molecular-weight polyethylene (UHMWPE)/multiwalled carbon nanotube (MWCNT) nanocomposites with different nanotube concentrations (0.5, 1.5, 2.5, and 3.5 wt %) were prepared via in situ polymerization with a novel, bisupported Ziegler-Natta catalytic system. Magnesium ethoxide [Mg(OEt) 2] and surface-functionalized MWCNTs were used as the support of the catalyst. Titanium tetrachloride (TiCl 4) accompanied by triethylaluminum constituted the Ziegler-Natta catalytic system. Preparation of the catalyst and the polymerization were carried out in the slurry phase under an argon atmosphere. Support of the catalyst on the MWCNTs was investigated with Fourier transform... 

Multi wall carbon nanotube (MWCNT) doped ZnO nanofibers were fabricated by electrospinning for the first time. We have successfully demonstrated the photocatalytic activity of doped nanofibers under visible light. Scanning electron microscopy showed that the diameter of MWCNT-doped ZnO nanofibers varied from 120 to 300 nm without agglomeration of MWCNT. Fourier transform infrared spectroscopy and X-ray diffraction studies proved the formation of ZnO bond and wurtzite structure with smaller crystal size in doped nanofibers. Raman spectra demonstrated slight shift in bond position after nanofiber doping, indicating the chemical bond between MWCNT and ZnO. X-ray photoelectron spectroscopy... 

Low-frequency O 2 plasma was used to modify the surface of polysulfone gas-separation membranes. The effects of the treatment time and plasma power input on the membranes were also investigated. Pure CO 2 and CH 4 gas-permeation measurements were performed before and after plasma treatment. The results show the increase of permeability of the treated membranes due to surface ablation and surface polarization up to 5.63 and 68.80 gas-permeation units for CH 4 and CO 2, respectively, whereas, the CO 2/CH 4 selectivity of the treated membranes varied from 7.7 to 45.3, depending on the treatment conditions. Attenuated total reflection-Fourier transform infrared spectroscopy determined the... 

Context: Elevated expression of the folate receptor (FR) occurs in many human malignancies. Thus, folate targeting is widely utilized in drug delivery purposes specially using nano-radioactive agents. Aims: In this work, we report production and biological evaluation of gallium-67 labeled superparamagnetic iron oxide nanoparticles, embedded by folic acid (67 Ga-SPION-folate) complex especially in tumor-bearing mice for tumor imaging studies. Settings and Design: The structure of SPION-folate was confirmed by X-ray diffraction (XRD), transmission electron microscopy (TEM) and foureir transform infrared spectroscopy (FT-IR) analyses. The radiolabeled SPION-folate formation was confirmed by... 

The main purpose of this study is to prepare and characterize hydroxyapatite (HA)-10%wt bioglass (BG) composite nanopowders and its bioactivity. Composites of hydroxyapatite with synthesized bioglass are prepared at various temperatures. Suitable calcination temperature is chosen by evaluating of the phase composition. X-ray diffraction (XRD), Transmission electron microscopy (TEM) and Scanning electron microscopy (SEM) techniques are utilized to characterize the prepared nanopowders. The bioactivity of the prepared composite samples is evaluated in an in vitro study by immersion of samples in simulated body fluid (SBF) for predicted time. Fourier transformed infrared (FTIR) spectroscopy and... 

Bone Tissue Engineering (BTE) composed of three main parts: scaffold, cells and signaling factors. Several materials and composites are suggested as a scaffold for BTE. Biocompatibility is one of the most important property of a BTE scaffold. In this work synthesis of a novel nanocomposite including layered double hydroxides (LDH) and gelatin is carried out and its biological properties were studied. The co-precipitation (pH=11) method was used to prepare the LDH powder, using calcium nitrate, Magesium nitrate and aluminum nitrate salts as starting materials. The resulted precipitates were dried. X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and scanning electron... 

CeO 2-TiO 2 nanoparticles were prepared by the sol-gel process using 2-hydroxylethylammonium formate as room-temperature ionic liquid and calcined at different temperatures (500-700°C). CeO 2-TiO 2-graphene nanocomposites were prepared by hydrothermal reaction of graphene oxide with CeO 2-TiO 2 nanoparticles in aqueous solution of ethanol. The photocatalysts were characterized by X-ray diffraction, BET surface area, diffuse reflectance spectroscopy, scanning electron microscopy, and Fourier transformed infrared techniques. The results demonstrate that the room-temperature ionic liquid inhibits the anatase-rutile phase transformation. This effect was promoted by addition of CeO 2 to TiO 2.... 

A simple bio-conjugation procedure to surround a single horseradish peroxidase (HRP) enzyme molecule with dendritic polyester macromolecules (polyester-32-hydroxyl-1-carboxyl bis-MPA dendron, generation 5) was proposed. The characterization of resultant nanoparticles entitled HRP dendrozyme, was performed by transmission electron microscopy, dynamic light scattering, gel permeation chromatography and Fourier transform infrared spectroscopy. The results showed that HRP nanoparticles were spherical in shape and have an average size of 14 ± 2. nm in diameter. Furthermore, bio-conformational characterization of HRP dendrozyme was performed by means of circular dichroism and fluorescence... 

Magnetite nanoparticles (mean particle size ranging from 10 to 20 nm) were prepared by a biomoleculeassisted solution-phase approach under ultrasonic irradiation. Cysteine was used as the capping agent in the solution. The results show that cysteine could be an efficient biocapping agent in producing Fe3O4 nanoparticles. The crystal structure and magnetic properties of the nanoparticles were characterized by XRD and VSM techniques, respectively. FT-IR was used to investigate the presence of cysteine on the nanoparticles surface. The influence of pH value of the solution on the size distribution and hydrodynamic size of nanoparticles were studied by TEM and DLS methods, respectively. The MTT... 

A novel nano-porous hydrogel (NPH) was synthesized via graft copolymerization of sodium acrylate (Na-AA) and acrylamide (AAm) onto salep backbones and its application as a carrier matrix for oral delivery of tetracycline hydrochloride (TH) was investigated. The Taguchi method as a strong experimental design tool was used for synthesis optimization. The swelling behavior of optimum hydrogel was measured in various media. The hydrogel formation was confirmed by Fourier transform infrared spectroscopy (FT-IR) and thermogravimetrical analysis (TGA). The study of the surface morphology of the hydrogels using SEM and AFM showed a nanoporous (average pore size: 180. nm) structure for the sample... 

The aim of this study was to investigate the thermal behavior of Mg-doped calcium phosphate compounds. Nanocrystalline HA and β-TCP mixtures containing different magnesium contents were synthesized via an alkoxide sol gel method. The ratio of (Ca+Mg)P was kept constant at 1.67, and the Mg content ranged between 0 and 3 mol%. The influence of magnesium on the phase composition, chemical structure, thermal behavior and morphological characteristics of nanopowders was analyzed using X-ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FT-IR), Simultaneous Thermogravimetry and Differential Thermal Analysis (STA/DTA), Scanning Electron Microscopy (SEM) and Transmission Electron... 

The significant role of protein nanoparticle interactions in nanomedicine and nanotoxicity is emerging recently through the identification of the nanoparticles (NP) protein (biomolecule) corona. The dynamic layer of proteins and/or other biomolecules adsorbed to the nanoparticle surface determines how a NP interacts with living systems and thereby modifies the cellular responses to the NP. Ehrenberg and co-workers used cultured endothelium cells as a model for vascular transport of polystyrene NP with various functional groups, which showed that the capacity of the various NP surfaces to adsorb proteins was indicative of their tendency to associate with cells. The quantification of the... 

Nanocrystalline TiO2-AgO thin films and powders were prepared by an aqueous particulate sol-gel route at the low temperature of 573 K (300 °C). Titanium tetraisopropoxide and silver nitrate were used as precursors, hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that the phase composition of the mixed oxide depends upon the annealing temperature, being a mixture of TiO2 and AgO in the range 573 K to 773 K (300 °C to 500 °C) and a mixture of TiO2, AgO, Ag2O at 973 K (700 °C). Furthermore, one of the smallest crystallite sizes was obtained for TiO... 

The suspension of titania nanoparticles in different alcohols (methanol, ethanol, and butanol) was prepared and triethanolamine (TEA) was used as a dispersant. The suspensions were characterized by different tests such as sedimentation, zeta potential, and Fourier transform infrared spectroscopy. The electrophoretic deposition (EPD) was performed at various voltages and times. EPD from butanolic suspension (0.8 g/L TEA) showed the slowest kinetics, because of the low electrophoretic mobility of titania nanoparticles in it (2.40 × 10-5 cm2·(V·s)-1). Also, it was observed that at low voltages (5, 10, and 20 V), the EPD kinetics from methanolic suspension (0 g/L TEA) was the fastest; however,... 

Nanostructured TiO2-ZrO2 thin films and powders were prepared by a straightforward aqueous particulate sol-gel route. Titanium (IV) isopropoxide and zirconium (IV) acetate hydrate were used as precursors, and hydroxypropyl cellulose was used as a polymeric fugitive agent in order to increase the specific surface area. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy revealed that the powder were crystallised at the low temperature of 500 °C, containing anatase-TiO 2 and tetragonal-ZrO2 phases. Furthermore, it was found that ZrO2 retarded the anatase-to-rutile transformation up to 900 °C. The activation energies for crystallite growth of TiO2 and ZrO2 components in... 

In this work, two important opioid antagonists, naltrexone and oxycodone, were prepared from thebaine and were characterized by IR, 1H NMR and 13C NMR spectroscopy. Moreover, computational NMR and IR parameters were obtained using density functional theory (DFT) at B3LYP/6-311++G* * level of theory. Complete NMR and vibrational assignment were carried out using the observed and calculated spectra. The IR frequencies and NMR chemical shifts, determined experimentally, were compared with those obtained theoretically from DFT calculations, showed good agreements. The RMS errors observed between experimental and calculated data for the IR absorptions are 85 and 105 cm-1, for the 1H NMR peaks are... 

Cadmium sulfide (CdS) nanowires and nanorods with different aspect ratios were successfully synthesized by the solvothermal method aided with various solvents, namely ethylenediamine, ethanolamine and triethylene tetraamine. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) analyses revealed that, highly pure CdS nanostructures were crystallized with different structures and preferable growth orientations depending on solvent nature. Field emission electron microscope (FE-SEM) images showed that the aspect ratio of CdS nanostructures depends upon the dielectric constant and boiling temperature of solvents. CdS nanostructures with the highest aspect ratio in the form... 

TiO2 nanorods have been successfully grown into a track-etched polycarbonate (PC) membrane by a particulate sol-electrophoretic deposition from an aqueous medium. The prepared sols had a narrow particle size distribution around 17 nm and excellent stability against aging, with zeta potentials in the range of 47-50 mV at pH 2. It was found that TiO2 nanorods were grown from dilute aqueous sol with a low, 0.1-M concentration. Fourier transform infrared spectroscopy (FT-IR) analysis confirmed that a full conversion of titanium isopropoxide was obtained by hydrolysis, resulting in the formation of TiO2 particles. X-ray diffraction (XRD) results revealed that TiO2 nanorods dried at 100 °C were a...