Among all active flow control methods, EHD, MHD and EMHD are the only methods which operate on the basis of body force induction on flow field. The EHD plasma actuator is the proper method which has been used in various flow control applications recently. In this paper, the effects of different body force fields on different domains have been studied for separation control on NACA 0021 and the results have been discussed. The airflow velocity has been assumed to be 35 m s-1 at a post-stall angle of attack of 23°. Three different domains have been used around the airfoil to investigate body forces with different strengths and directions and those which give the best result in separation... 

This study investigates the efficient removal of ciprofloxacin (Cip) and cephalexin (Cep) using magnetic graphene oxide (Fe3O4/GO) as an adsorbent. To this end, the magnetic nanocomposite was synthesized via a co-precipitation method. The surface and properties of the adsorbent were characterized using pHpzc, XRD, FE-SEM, FT-IR, VSM, and TEM techniques. The XRD and FT-IR results were consistent with those of previous results. The FE-SEM and TEM results of the synthesized nanoparticles were less than 30 nm in size and showed a spherical shape. The maximum saturation magnetization of the Fe3O4/GO nanocomposite was 45.97 emu g−1. Also, the pHpzc of the nanocomposite was 6.2. The optimal... 

Interactions between the metal interconnect and glass sealant in the solid oxide cells stack are critical to retaining the system integrity. To address this issue, in the current study, 8YSZ coating is applied on the Crofer22 APU steel via sol-gel and dip-coating method. Dense and continuous 8YSZ coatings are obtained on Crofer22 APU substrates. X-ray diffraction and Raman spectroscopy results show that both cubic and tetragonal structures of 8YSZ are formed. A glass-based sealing paste is applied on bare and 8YSZ coated Crofer22 APU steel. The interfacial compatibility and chemical stability of steel/glass and steel/8YSZ/glass joint couples are investigated using SEM and EDS line scan... 

High strength Al-AlN composites were synthesized via high-energy milling and sintering technique. Al-X wt.% AlN (X = 0, 2.5, 5 and 10) composite powders were milled in a planetary ball mill for 25 h. Morphology, particle size distribution, crystallite size, micro-strain, and microhardness of milled powders were studied. Ball-milled powders were degassed at 400 °C for 30 min. After uniaxial cold compaction, composite compacts were sintered at 650 °C for 20, 30 and 60 min under N2 atmosphere. Effects of reinforcement content, degassing treatment and sintering time on the sinterability of powders were investigated. The results revealed that the sinterability was degraded by increasing the... 

Abstract: The effect of de-siliconization on the oxidation behavior of AISI 430 stainless steel used for solid oxide fuel cell interconnect application was investigated. De-siliconization treatment was conducted via heating steel parts in an H2 environment. The de-siliconized substrates were then coated with a Mn1.5Co1.5O4 spinel coating, using wet spray method. For comparison, a similar coating process was applied on the as-received AISI 430 stainless steel specimens. Oxidation kinetics of coated interconnects were evaluated at 700, 800 and 900 °C in air. Results showed that the de-siliconization surface treatment decreased oxidation rates, with kinetic rates (g2 cm−4 s−1) of 4.39 × 10−14... 

In this paper we examine demodulation methods for nonuniform Pulse Position Modulation (PPM), which is generated by the crossings of a modulating signal with a sawtooth wave. Here, we are interested in PPM at the Nyquist rate and illustrate the efficiency of the iterative methods. Several iterative methods such as Wiley/Marvasti, Time-varying, adaptive weight, Zero-order-hold, Voronoi, linear interpolation algorithms are discussed, where the PPM demodulation is converted as a nonuniform sampling reconstruction problem. Also another approach called the inverse system approach is introduced and the performance of the two algorithms is assessed. © Springer-Verlag 2004  

Assessment of mechanical properties of glass/metal joints is a challenging process, especially when the application relevant conditions of the joints have to be considered in the test design. In this study, a finite element method (FEM) is implemented to analyze a torsional shear strength test designed for glass-ceramic/steel joints aiming towards solid oxide fuel/electrolysis cells application. Deviations from axial symmetry of the square flanges (ends) of respective hourglass-shaped specimens and also supporting and loading sockets of the test set-up are included in the model to simulate conditions close to reality. Undesirable tensile stress and also shear stress concentration appear at... 

The structural integrity of the sealant is critical for the reliability of solid oxide cells (SOCs) stacks. In this study, elastic modulus (E), hardness (H) and fracture toughness (KIC) of a rapid crystallizing glass of BaO–CaO–SiO2 system termed “sealant G” are reported as determined using an indentation test method at room temperature. A wide range of indentation loads (1 mN–10 N) was used to investigate the load-dependency of these mechanical properties. Values of 95 ± 12 GPa, 5.8 ± 0.2 GPa and 1.15 ± 0.07 MPa m0.5 were derived for E, H and KIC using the most suitable indentation loads. An application relevant annealing treatment of 500 h at 800 °C does not lead to a significant change of... 

The structural integrity of the sealant is critical for the reliability of solid oxide cells (SOCs) stacks. In this study, elastic modulus (E), hardness (H) and fracture toughness (KIC) of a rapid crystallizing glass of BaO–CaO–SiO2 system termed “sealant G” are reported as determined using an indentation test method at room temperature. A wide range of indentation loads (1 mN–10 N) was used to investigate the load-dependency of these mechanical properties. Values of 95 ± 12 GPa, 5.8 ± 0.2 GPa and 1.15 ± 0.07 MPa m0.5 were derived for E, H and KIC using the most suitable indentation loads. An application relevant annealing treatment of 500 h at 800 °C does not lead to a significant change of... 

The conventional relations for calculating the fracture stresses consider only elastic deformation but ignore viscoelastic and viscoplastic behaviors. Measuring the joining strength of a composite glass sealant-metallic interconnect specimen at solid oxide cell application relevant at high temperatures is a case where such effects can become significant. In the current study, three-point and four-point bending test results were analyzed using the finite element method (FEM) to assess systematic and random errors. It is shown that plastic deformation of the steel interconnect material at high temperature, although having a large effect on the stress distribution in the... 

In this study, a method for enhancing low-contrast images is proposed. This method, called Gaussian mixture model-based contrast enhancement (GMMCE), brings into play the Gaussian mixture modelling of histograms to model the content of the images. On the basis of the fact that each homogeneous area in natural images has a Gaussian-shaped histogram, it decomposes the narrow histogram of low-contrast images into a set of scaled and shifted Gaussians. The individual histograms are then stretched by increasing their variance parameters, and are diffused on the entire histogram by scattering their mean parameters, to build a broad version of the histogram. The number of Gaussians as well as their... 

High-energy milling technique was used to synthesize Al-10 wt.%AlN-nanostructured composite powder in a planetary ball-mill under argon atmosphere up to 25 h. To show the role of AlN particles, process was conducted for monolithic aluminum. The changes in powder characteristics were investigated by time. Microstructure of powders was studied after different milling times by scanning electron microscope (SEM). The morphological evolutions showed that relative equiaxed powder could be synthesized after 25 h milling. Structural analysis was performed by X-ray diffraction method (XRD) to determine the grain sizes and lattice strain. Furthermore, particle size analysis (PSA) revealed the... 

The compressibility behavior of Al-AlN nanostructured composite powder with different amount of reinforcement content was studied. The composite powder was synthesized by blending and high-energy milling process for 25 h. Williamson-Hall method was applied to determine the crystallite size after milling process. To investigate the role of reinforcement particles in consolidation of composite powders, monolithic aluminum powder was examined. Samples were made at different pressures and relationships were established between the compaction pressure and the density of the compacts. The modified Heckel equation was used to assume the pressure effect on yield strength and then was compared with... 

Electrophoretic technique was used to deposit micro- and nano-sized aluminum nitride coatings on stainless steel surfaces by using a well-dispersed stable suspension produced by addition of AlN powder plus a small amount of iodine to ethanol. Parabolic regime governed the deposition. Electrophoretic deposition for 240 s at 100 V resulted in formation of a uniformly dense film on the top, but a porous inhomogeneous layer at the bottom. This was attributed to fast deposition of coarse particles and/or agglomerates at large electric fields. After drying, micro-sized particles led to a uniform crack-free interface while nano-particles resulted in fragmented non-cohesive layers. Weight loss... 

Compressibility of a nanostructured Al-5AlN composite powder synthesised via high energy ball milling for various times was studied by means of a modified Heckel equation. Since workhardening and morphological changes take place by milling evolution, the compressibility was consequently affected. Strengthening of composite compacts was influenced by milling and compaction processes, i.e. strength of compacts increased at longer milling times and higher compaction pressures. It was found that, at the initial stages of milling and higher compaction pressures, the strengthening was mostly affected from compaction process, whereas the milling strengthening fraction was near to unity at lower...